Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 8.00 - 165 MPa | 1160 - 23900 psi | Average value: 50.5 MPa Grade Count:86 |
Overview of materials for Polybutylene Terephthalate (PBT), Unreinforced, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Unreinforced, Molded". Each property range of values reported is minim.. |
|||
Tensile Strength, Ultimate | 8.00 MPa | 1160 psi | ASTM D638 |
ExxonMobil Optema® TC-221 Ethylene Methyl Acrylate for Compounding
(discontinued **) Data provided by the manufacturer, Exxon Chemical.27% Methyl Acrylate. An Ethylene Methyl Acrylate copolymer which can be used for making alloys, blends, and compounds, or be injection molded where.. |
|||
Tensile Strength, Ultimate | 8.00 MPa | 1160 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman 18BOA Polyethylene
(discontinued **) Polyethylene 18BOA is a low density formulation used for injection molding. It is an outstanding material for molding lids and other container closures because it processes easily on automatic mold.. |
|||
Tensile Strength, Ultimate | 8.00 MPa | 1160 psi | 500 mm/min (20 in./min.); Type IV Specimen; ASTM D638 |
Eastman 18DOA Polyethylene
(discontinued **) Polyethylene 18DOA is a low density formulation suggested for the production of closures where a high melt index material is needed to meet shrinkage requirements and fast molding cycles. It molds .. |
|||
Tensile Strength, Ultimate | 8.00 MPa | 1160 psi | 500 mm/min (20 in./min.); Type IV Specimen; ASTM D638 |
Eastman Voridian D4009-A Polyethylene
(discontinued **) Voridian polyethylene D4009-A is a low density formulation used for injection molding. It is an outstanding material for molding lids and other container closures because it processes easily on aut.. |
|||
Tensile Strength, Ultimate | 8.00 MPa | 1160 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman D4044A Polyethylene
(discontinued **) D4044-A is a low density formulation used for injection molding. It is an outstanding material for molding lids and other container closures because it processes easily on automatic molding equipme.. |
|||
Tensile Strength, Ultimate | 8.00 MPa | 1160 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman Voridian D4053-A Polyethylene
(discontinued **) Voridian polyethylene D4053-A is a low density formulation used for injection molding. It is an outstanding material for molding lids and other container closures because it processes easily on aut.. |
|||
Tensile Strength, Ultimate | 8.00 MPa | 1160 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman Voridian E6838-010A Polyethylene
(discontinued **) Voridian polyethylene E6838-010A is a low density formulation with medium slip used for injection molding. It is an outstanding material for molding lids and other container closures because it pro.. |
|||
Tensile Strength, Ultimate | 8.00 - 15.0 MPa @Temperature 60.0 - 90.0 °C |
1160 - 2180 psi @Temperature 140 - 194 °F |
Average value: 11.5 MPa Grade Count:1 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant". Each property range of values rep.. |
|||
Tensile Strength, Ultimate | 8.00 - 60.0 MPa @Temperature 60.0 - 90.0 °C |
1160 - 8700 psi @Temperature 140 - 194 °F |
Average value: 29.6 MPa Grade Count:3 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled". Specific grades with glass content betwe.. |
|||
Tensile Strength, Ultimate | 8.00 MPa | 1160 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman M3018-P Polyethylene
(discontinued **) Low density polyethylene M3018-P is a specialty formulation suggested for low temperature extrusion coating applications. M3018-P has been found to exhibit good coatability and adhesion to various .. |
|||
Tensile Strength, Ultimate | 8.00 - 39.0 MPa | 1160 - 5660 psi | Average value: 17.0 MPa Grade Count:18 |
Overview of materials for Polytetrafluoroethylene (PTFE), Conductive Carbon Filled This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Conductive Carbon Filled". Each property range of values reported is min.. |
|||
Tensile Strength, Ultimate | 8.00 MPa | 1160 psi | ISO R527-1 |
LyondellBasell Hifaxâ„¢ CA45 Thermoplastic Olefin Resin Key Features: medium melt flow, medium modulus thermoplastic elastomeric olefin resin, excellent balance of properties, excellent processability, good colorability, excellent surface appearanceAppli.. |
|||
Tensile Strength, Ultimate | 8.00 MPa | 1160 psi | DIN 53504 |
Lubrizol ESTANE® T4065 Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 8.00 MPa | 1160 psi | |
Dow Corning SILASTIC® 9220/55 KIT PARTS A&B 55 Durometer, 2-part, 1 to 1 mix, black Liquid Silicone Rubber.Information provided by Dow Corning |
|||
Tensile Strength, Ultimate | 8.000 MPa | 1160 psi | |
Dow Corning SILASTIC® 9412/30E KIT PARTS A&B 30 Durometer, 2-part, 1 to 1 mix, 2-part, 1 to 1 mix, opaque, Auto connector seal grade, Liquid Silicone Rubber.Information provided by Dow Corning |
|||
Tensile Strength, Ultimate | 8.00 MPa | 1160 psi | |
Dow Corning SILASTIC® Q7-4765 BIOMEDICAL GRADE ETR ELASTOMER, KIT Two-part, platinum-catalyzed (1:1 by weight), enhanced tear-resistant silicone elastomers are heat cured high consistency silicone rubbers designed for use by customers fabricating medical devices.I.. |
|||
Tensile Strength, Ultimate | 8.00 MPa | 1160 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
Dow Nordel® IP 4725P Dense Extrusion FormulationNordel® IP 4725P |
|||
Tensile Strength, Ultimate | 8.00 - 24.0 MPa | 1160 - 3480 psi | |
ATG s.r.l. HNBR Hydrogenated Nitrile Butadiene Rubber |
|||
Tensile Strength, Ultimate | 8.00 - 23.0 MPa | 1160 - 3340 psi | |
ATG s.r.l. XNBR Carboxylated Nitrile Rubber |
|||
Tensile Strength, Ultimate | 8.00 MPa | 1160 psi | cured 7 days @ 25°C |
Abatron AboCast 8110-2/AboCure 8110-3 Flexible Epoxy This epoxy system can achieve flexibility and plasticity without sacrificing adhesive, electrical, structural, and other properties. This compound is a clear (unfilled) basic formulation. Its applic.. |
|||
Tensile Strength, Ultimate | 8.00 MPa @Temperature 250 °C |
1160 psi @Temperature 482 °F |
ASTM D638 |
Asahi Glass Fluon® P-63P PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
Tensile Strength, Ultimate | 8.00 MPa @Temperature 250 °C |
1160 psi @Temperature 482 °F |
ASTM D638 |
Asahi Glass Fluon® P-810UP PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
Tensile Strength, Ultimate | 8.00 MPa | 1160 psi | ASTM D638 |
Global S-1018 Low Density Polyethylene, Injection Molding Grade
(discontinued **) Description-transparency, high toughness, flexibility, high impact strength, good chemical resistanceApplications-packagingMeets FDA requirements as listed in food additives regulation 21 CFR 117.15.. |
|||
Tensile Strength, Ultimate | 8.00 MPa | 1160 psi | ASTM D638 |
Huntsman PE2050 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: High flow characteristics, good gloss, and processability.Applications: Injection molding: large moldings including housewares and toys.FDA Notes: Conforms to.. |
|||
Tensile Strength, Ultimate | 8.00 MPa | 1160 psi | ASTM D638 |
Huntsman PE2080 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Very high flow rapid set-up characteristics, excellent clarity, and gloss.Applications: Injection molding: lids and difficult to fill applications.FDA Notes: .. |
|||
Tensile Strength, Ultimate | 8.00 - 9.00 MPa | 1160 - 1310 psi | Average value: 8.50 MPa Grade Count:4 |
Overview of materials for Low Density Polyethylene (LDPE), Masterbatch Grade This property data is a summary of similar materials in the MatWeb database for the category "Low Density Polyethylene (LDPE), Masterbatch Grade". Each property range of values reported is minimum a.. |
|||
Tensile Strength, Ultimate | 8.00 - 8.00 MPa @Temperature 120 - 120 °C |
1160 - 1160 psi @Temperature 248 - 248 °F |
Average value: 8.00 MPa Grade Count:1 |
Overview of materials for Cellulose Acetate Propionate, Molded This property data is a summary of similar materials in the MatWeb database for the category "Cellulose Acetate Propionate, Molded". Each property range of values reported is minimum and maximum val.. |
|||
Tensile Strength, Ultimate | 8.00 - 13.0 MPa | 1160 - 1890 psi | Average value: 10.2 MPa Grade Count:7 |
Overview of materials for Ethylene-Methyl Acrylate Copolymer, Compounding Grade This property data is a summary of similar materials in the MatWeb database for the category "Ethylene-Methyl Acrylate Copolymer, Compounding Grade". Each property range of values reported is minimu.. |