SABIC Innovative Plastics NORYL EM7100 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL EM7100 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Automotive interiors. 200F DTUL. Excellent processability/economy. Good impact/mechanicals vs styrenics. Trim/instrument panel components.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 48 % | 48 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 62.0 MPa | 8990 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 3.47 J/cm | 6.50 ft-lb/in | ASTM D256 |
| 1.60 J/cm @Temperature -40.0 °C |
3.00 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 30.0 J | 22.1 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 11.0 J @Temperature -30.0 °C |
8.11 ft-lb @Temperature -22.0 °F |
Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 73.8 µm/m-°C @Temperature 0.000 - 100 °C |
41.0 µin/in-°F @Temperature 32.0 - 212 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C @Thickness 6.40 mm |
214 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C @Thickness 6.40 mm |
208 °F @Thickness 0.252 in |
unannealed; ASTM D648 |