- SABIC Innovative Plastics Cycolac® MG34LG ABS
SABIC Innovative Plastics Cycolac® MG34LG ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® MG34LG ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Automotive: Low gloss ABS for unpainted interior applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.0 % | 1.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 6.0 g/10 min @Load 3.80 kg, Temperature 200 °C |
6.0 g/10 min @Load 8.38 lb, Temperature 392 °F |
ASTM D1238 |
| Melt Index of Compound | 24 g/10 min @Load 10.0 kg, Temperature 220 °C |
24 g/10 min @Load 22.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 31.0 MPa | 4500 psi | 5 mm/min; ISO 527 |
| 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | 5 mm/min; ISO 527 |
| 40.0 MPa | 5800 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 25 % | 25 % | Type I, 5 mm/min; ASTM D638 |
| 25.7 % | 25.7 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 2.1 % | 2.1 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.13 GPa | 309 ksi | 5 mm/min; ASTM D638 |
| 2.26 GPa | 328 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 62.0 MPa | 8990 psi | 2 mm/min; ISO 178 |
| 68.0 MPa | 9860 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.06 GPa | 299 ksi | 2 mm/min; ISO 178 |
| 2.20 GPa | 319 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 2.45 J/cm | 4.59 ft-lb/in | ASTM D256 |
| 0.420 J/cm @Temperature -30.0 °C |
0.787 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | 80*10*4; ISO 180/1A |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.80 J/cm² | 8.57 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 35.0 J @Temperature 23.0 °C |
25.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 93.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
52.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 93.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
52.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 93.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
52.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 93.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
52.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C | 178 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 82.0 °C @Thickness 3.20 mm |
180 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 97.0 °C | 207 °F | Rate B/50; ISO 306 |
| 98.0 °C | 208 °F | Rate B/50; ASTM D1525 | |
| 101 °C | 214 °F | Rate B/120; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | PASSES | IEC 60695-10-2 |