SABIC Innovative Plastics LNP Thermocomp FF006 PE

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp FF006 PE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP Thermocomp FF-1006 is a glass filled Polyethylene.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
1.18 g/cc
0.0426 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.030 %
0.030 %
23°C / 50% RH; ISO 62
0.020 %

@Time 86400 sec
0.020 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Time 86400 sec
0.0040 - 0.0070 in/in

@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm

@Time 86400 sec
0.010 - 0.030 in/in

@Time 24.0 hour
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 44.0 MPa
6380 psi
Type I, 5 mm/min; ASTM D 638
44.0 MPa
6380 psi
5 mm/min; ISO 527
Tensile Strength, Yield 44.0 MPa
6380 psi
Type I, 5 mm/min; ASTM D 638
44.0 MPa
6380 psi
5 mm/min; ISO 527
Elongation at Break 1.4 %
1.4 %
5 mm/min; ISO 527
1.5 %
1.5 %
Type I, 5 mm/min; ASTM D 638
2.1 %
2.1 %
Flexural Strain, 2 mm/min; ISO 178
Elongation at Yield 1.4 %
1.4 %
5 mm/min; ISO 527
1.5 %
1.5 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 4.58 GPa
664 ksi
1 mm/min; ISO 527
6.66 GPa
966 ksi
50 mm/min; ASTM D 638
Flexural Strength 47.0 MPa
6820 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Yield Strength 62.0 MPa
8990 psi
1.3 mm/min, 50 mm span; ASTM D 790
64.0 MPa
9280 psi
2 mm/min; ISO 178
Flexural Modulus 4.21 GPa
611 ksi
1.3 mm/min, 50 mm span; ASTM D 790
4.94 GPa
716 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.550 J/cm

@Temperature 23.0 °C
1.03 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 1.75 J/cm

@Temperature 23.0 °C
3.28 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Temperature 23.0 °C
1.90 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 12.0 kJ/m²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 32.2 µm/m-°C

@Temperature 23.0 - 60.0 °C
17.9 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
32.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
17.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 125 µm/m-°C

@Temperature 23.0 - 60.0 °C
69.4 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
125 µm/m-°C

@Temperature -40.0 - 40.0 °C
69.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 129 °C
264 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
130 °C

@Thickness 3.20 mm
266 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 111 °C
232 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
115 °C

@Thickness 3.20 mm
239 °F

@Thickness 0.126 in
unannealed; ASTM D 648