Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 20.7 MPa | 3000 psi | Type I, 51 mm/min; ASTM D638 |
PolyOne Maxxam™ MD 4245-59770 Polypropylene Copolymer (PP Copolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | Type I, 51 mm/min; ASTM D638 |
PolyOne Maxxam™ PPC-20C Nat Polypropylene Copolymer (PP Copolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
Omni Plastics OmniTech™ CPP XE72-A BK17 ESD Polypropylene Conductive OmniTech™ is a family of non-standard products custom developed for applications with unique functional requirements, including but not limited to: Flame Retardant, Conductive, Wear Resistant, and .. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
Omni Plastics OmniTuff™ HPP CCF30 Homopolymer Polypropylene Calcium Carbonate Filled Applications: Structural parts across industry segments including pump housings, wheels, handles, mountings, brackets, levers, pressure vessels, and furniture components.Information provided by Omni.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | TM R050-36 |
Resinlab® EP965 Clear Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP965 Clear is a two part unfilled electronic grade epoxy encapsulant designed for medium sized castings. It cures at room temperature to a tough, semi-rigid polymer. It has good wetting .. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | 50 mm/min; ISO 527 |
Phillips Sumika Marlex® CHP-370 Thermoplastic Polyolefin
(discontinued **) Thermoplastic Polyolefin, Good Stiffness and Impact PerformanceApplications: Automotive Pillar TrimConditioning after Molding: 48 hr at 23°CNominal Shrinkage: 0.8-1.0%Drying conditionsTemperature: .. |
|||
Tensile Strength, Yield | 20.7 - 58.3 MPa | 3000 - 8450 psi | Average value: 44.5 MPa Grade Count:118 |
Overview of materials for Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded". Each property range of values reported is m.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
Fiberfil® PP-60/VO/NH Polypropylene Homopolymer, Flame Retardant, non-halogenated, UL94 V0 Information provided by FIBERFIL Engineered Plastics |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
LyondellBasell Petrothene® LR686001 High Density Polyethylene ApplicationsPETROTHENE LR686001 is designed for use as insulation for foam/skin telephone singles, and is a natural, expandable, high density polyethylene compound containing a chemical blowing agen.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
Techmer ES HiFill® PP 0121 B Polypropylene Availability: North AmericaForms: PelletsFiller/Reinforcement: Unspecified Filler/ReinforInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | >= 20.7 MPa | >= 3000 psi | ASTM D-882 |
Saint-Gobain Norton® T-100 Virgin Skived PTFE Film (0.003" thick) T-100/T-200 Features/Benefits: Outstanding heat and chemical resistance; High dielectric strength; Anti-stick properties; Can be chemically etched for bondability; Applications include laminate rele.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D412 |
Teknor Apex APEX® 3201-90 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Automotive Applications, Non-specific Food Applications, General Purpose, Medical Applications, Modeling.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D412 |
Borealis Visico™/Ambicat™ ME4425/LE4472 Ambient Curing, Moisture-Crosslinking Polyethylene Compound for Low Voltage Insulation Visico LE4423 is a natural, ethylene vinyl silane copolymer that, when combined with the catalyst masterbatch Ambicat LE4472, will undergo an accelerated, moisture-induced crosslinking reaction. Th.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 1010-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1010-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristics .. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 293 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP293 is an injection molding grade olefinic thermoplastic elastomer. This product is recommended for parts requiring excellent low temperature impact properties with good dim.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 293 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP293 is an injection molding grade olefinic thermoplastic elastomer. This product is recommended for parts requiring excellent low temperature impact properties with good dim.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 1010-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1010-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristics .. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 293 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP293 is an injection molding grade olefinic thermoplastic elastomer. This product is recommended for parts requiring excellent low temperature impact properties with good dim.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
A. Schulman PP 1188-01 Polypropylene Extra High-Impact Polypropylene DescriptionPolypropylene PP 1188-01 is an extra high-impact polypropylene, copolymer type, with excellent low temperature properties. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
A. Schulman POLYTROPE™ CB 1010U-330 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope CB 1010U-330 is a color matched/color blended injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properti.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 1010-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1010-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristics .. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | |
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 82A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
Dow C702-20 Polypropylene Impact Copolymer Resin OverviewHigh impactComplies with: U.S. FDA FCN 843, Canadian HPFB No ObjectionDOW C702-20 Polypropylene Resin is intended for use in injection molded applications requiring high impact. It is parti.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | |
Dow HDPE 08454N High Density Polyethylene DOW HDPE 08454N resin is a narrow molecular weight distribution copolymer designed to offer excellent impact strength and toughness, with good stiffness. This resin has good processability over a wi.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D-638 |
Bapolan® 6409 Polystyrene, Injection Grade Bapolan PS6409 is designed for injection molding applications requiring superior impact and gloss. It complies with US FDA21 CFR177.1640 and 94HB UL rating.Application: General purpose.Bapolene® a.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D-638 |
Axiall 19450 Wire & Cable Flexible PVC 105°C rated insulation compound with very good migration and oil resistance. Recommended for toner resistant applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D-638 |
Axiall H 3182A Plenum Flexible PVC Plenum-grade insulation compound for Category 3 applications. UL QMTM2 plenum cable compound component.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | |
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 82A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D-638 |
Axiall 28930 Coax & Telecom Flexible PVC Non-lead stabilized 105C FT-4 riser jacket compound. UV resistant.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | TM R050-36 |
Resinlab® EP1310 Medium Reactivity Epoxy Encapsulant Resinlab™ EP1310 is a two part medium reactivity epoxy encapsulant capable of being quickly gelled prior to full cure by exposing to a UV light source. Usually 5- 10 seconds is sufficient to gel th.. |