PolyOne Maxxam™ PPC-20C Nat Polypropylene Copolymer (PP Copolymer)

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer
Manufacturer PolyOne Corporation
Trade Name Maxxam™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Maxxam™ PPC-20C Nat Polypropylene Copolymer (PP Copolymer).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium carbonate, glass and talc to provide a desired balance of properties including stiffness, durability, impact resistance and heat resistance. Custom grades are available with features such as UV stabilizers, heat stabilizers, custom color, high impact, etc.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.04 g/cc
1.04 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.011 - 0.015 cm/cm
0.011 - 0.015 in/in
ASTM D955
Melt Flow 8.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
8.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
Procedure A; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 75
75
ASTM D785
Tensile Strength, Yield 20.7 MPa
3000 psi
Type I, 51 mm/min; ASTM D638
Elongation at Break 280 %
280 %
Type I, 51 mm/min; ASTM D638
Flexural Strength 24.8 MPa
3600 psi
ASTM D790
Flexural Modulus 1.45 GPa
210 ksi
ASTM D790
Izod Impact, Notched 0.850 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
1.59 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Gardner Impact 20.8 J

@Thickness 3.18 mm,
Temperature -23.0 °C
15.3 ft-lb

@Thickness 0.125 in,
Temperature -9.40 °F
ASTM D3029
Dart Drop Total Energy 7.79 J/cm
0.0146 ft-lb/mil
Energy to Maximum Load; ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 82.8 °C

@Thickness 3.18 mm
181 °F

@Thickness 0.125 in
Unannealed; ASTM D648
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
ALL; UL 94
Processing Properties Metric English Comments
Mold Temperature 16.0 - 50.0 °C
60.8 - 122 °F
Descriptive Properties Value Comments
Additive Impact Modifier
Appearance Natural Color
Features Copolymer
General Purpose
Impact Modified
Filler / Reinforcement Calcium Carbonate Filler
Unspecified FillerReinfor., 20% Filler by Weight
Forms Pellets
Generic Material PP Copolymer
Generic Name Polypropylene Copolymer (PP Copolymer)
Processing Method Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Uses Automotive Applications
Construction Applications
Consumer Applications
General Purpose
Industrial Applications