Resinlab® EP1310 Medium Reactivity Epoxy Encapsulant

Category Polymer , Thermoset , Epoxy , Epoxy Encapsulant, Unreinforced
Manufacturer Resinlab®
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Resinlab® EP1310 Medium Reactivity Epoxy Encapsulant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Resinlab™ EP1310 is a two part medium reactivity epoxy encapsulant capable of being quickly gelled prior to full cure by exposing to a UV light source. Usually 5- 10 seconds is sufficient to gel the top layer of the product. Full cure will occur over time at room temperature even in shadow areas. Due to the acrylate reaction, the catalyzed resin warms slightly to about 32oC nearly instantaneously.Information Provided by Resinlab L.L.C., an Ellsworth Adhesives Company.
Physical Properties Metric English Comments
Specific Gravity 1.03 g/cc
1.03 g/cc
Part B; TM R050-16
1.10 g/cc
1.10 g/cc
Mixed; TM R050-16
1.14 g/cc
1.14 g/cc
Part A; TM R050-16
Water Absorption 0.30 %

@Time 86400 sec
0.30 %

@Time 24.0 hour
TM R050-35
Viscosity 1500 cP
1500 cP
Part B, RVT, #2, 20 rpm; TM R050-12
3000 cP
3000 cP
Mixed; TM R050-12
3500 cP
3500 cP
Part A, RVT, #3, 20 rpm; TM R050-12
Mechanical Properties Metric English Comments
Hardness, Shore D 80
80
TM R050-17
Tensile Strength at Break 31.0 MPa
4500 psi
TM R050-36
Tensile Strength, Ultimate 31.7 MPa
4600 psi
TM R050-36
Tensile Strength, Yield 20.7 MPa
3000 psi
TM R050-36
Elongation at Break 2.0 - 3.0 %
2.0 - 3.0 %
TM R050-36
Tensile Modulus 2.07 GPa
300 ksi
TM R050-36
Compressive Yield Strength 41.4 MPa
6000 psi
TM R050-38
Compressive Strength 103 MPa
15000 psi
Break; TM R050-38
138 MPa
20000 psi
Ultimate; TM R050-38
Compressive Modulus 2.07 GPa
300 ksi
TM R050-38
Adhesive Bond Strength 20.7 MPa
3000 psi
Lap shear; 2024 T3 Al Abraded / MEK Wipe; TM R050-37
Thermal Properties Metric English Comments
CTE, linear 55.0 µm/m-°C
30.6 µin/in-°F
Thermal Conductivity 0.140 W/m-K
0.972 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air 150 °C
302 °F
Minimum Service Temperature, Air -40.0 °C
-40.0 °F
Glass Transition Temp, Tg 54.0 °C
129 °F
TM R050-25
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+13 ohm-cm
2.00e+13 ohm-cm
Dielectric Constant 4.5

@Frequency 100 Hz,
Temperature 25.0 °C
4.5

@Frequency 100 Hz,
Temperature 77.0 °F
Dielectric Strength 17.3 kV/mm
440 kV/in
Processing Properties Metric English Comments
Pot Life 15 - 30 min
15 - 30 min
Mass: 50g; TM R050-19
Descriptive Properties Value Comments
Color Clear
Mix Ratio 2:1
Volume
215:100
Weight