BASF Ultramid® 8231G HS 14% Glass Filled PA6 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8231G HS 14% Glass Filled PA6 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8231G HS is a heat stabilized, 14% glass fiber reinforced nylon 6 injection molding compound. It is also available in non-heat stabilized (Ultramid 8231) and/or pigmented versions. The glass fiber reinforcement enhances performance such as strength, stiffness and heat deflection temperature. The heat stabilizer system extends the properties at elevated temperatures. It also has excellent chemical resistance to greases, oils and hydrocarbons. njection molding compound possessing a balance of engineering properties combined with excellent processability and surface aesthetics.
Physical Properties Metric English Comments
Density 1.067 g/cc
0.03855 lb/in³
Melt; ISO 1183
1.23 g/cc
0.0444 lb/in³
dry; ISO 1183
Water Absorption 1.4 %
1.4 %
24 hour; ISO Test
8.1 %
8.1 %
beginning dry; ISO 62
Moisture Absorption at Equilibrium 2.3 %
2.3 %
beginning dry (23°C/50% R.H.); ISO 62
Viscosity Measurement 50
50
Formic Acid
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength at Break 79.0 MPa
11500 psi
0.2 in/min; ASTM Test
20.0 MPa

@Temperature 80.0 °C
2900 psi

@Temperature 176 °F
ISO Data
20.0 MPa

@Temperature 80.0 °C
2900 psi

@Temperature 176 °F
ASTM Test
40.0 MPa

@Temperature 120 °C
5800 psi

@Temperature 248 °F
ISO Data
40.0 MPa

@Temperature 120 °C
5800 psi

@Temperature 248 °F
ASTM Test
170 MPa

@Temperature -40.0 °C
24700 psi

@Temperature -40.0 °F
ASTM Test
170 MPa

@Temperature -40.0 °C
24700 psi

@Temperature -40.0 °F
ISO Data
Tensile Strength, Ultimate 80.0 MPa
11600 psi
5mm/min; ISO 527
Elongation at Break 9.0 %
9.0 %
5mm/min; ISO 527
9.0 %
9.0 %
0.2 in/min; ASTM Test
4.0 %

@Temperature -40.0 °C
4.0 %

@Temperature -40.0 °F
ASTM Test
4.0 %

@Temperature -40.0 °C
4.0 %

@Temperature -40.0 °F
ISO Data
6.0 %

@Temperature 120 °C
6.0 %

@Temperature 248 °F
ISO Data
6.0 %

@Temperature 120 °C
6.0 %

@Temperature 248 °F
ASTM Test
15 %

@Temperature 80.0 °C
15 %

@Temperature 176 °F
ASTM Test
15 %

@Temperature 80.0 °C
15 %

@Temperature 176 °F
ISO Data
Tensile Modulus 2.64 GPa
383 ksi
1mm/min; ISO 527
1.90 GPa

@Temperature 120 °C
276 ksi

@Temperature 248 °F
ISO Data
2.30 GPa

@Temperature 80.0 °C
334 ksi

@Temperature 176 °F
ISO Data
6.60 GPa

@Temperature -40.0 °C
957 ksi

@Temperature -40.0 °F
ISO Data
Flexural Strength 65.0 MPa
9430 psi
ISO Data
101 MPa
14600 psi
ASTM Test
219 MPa

@Temperature -40.0 °C
31800 psi

@Temperature -40.0 °F
ASTM Test
Flexural Modulus 2.21 GPa
321 ksi
ISO Data
2.40 GPa
348 ksi
ASTM Test
Thermal Properties Metric English Comments
Specific Heat Capacity 2.728 J/g-°C
0.6520 BTU/lb-°F
Melt
Thermal Conductivity 0.230 W/m-K
1.60 BTU-in/hr-ft²-°F
Melt
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Electrical Properties Metric English Comments
Comparative Tracking Index 400 V
400 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 275 °C
527 °F
Injection molding
Mold Temperature 95.0 °C
203 °F
Injection molding
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat
UL.UL-C Yes