SABIC Innovative Plastics NORYL WCD801AU PPE-TPE (Asia Pacific)
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL WCD801AU PPE-TPE (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flexible, UV stabilized, halogen free extrusion grade for applications such as wire insulation and cable jacket. Good color stability after UV weathering per ASTM D4459. Light color capable. Flame retardant performance capable of meeting UL VW-1 requirement. 80C application temperature rating and good heat deformation performance as defined by UL 1581. 82 Shore A hardness. Processing typically conducted on standard extrusion equipment. UL 1581 tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 - 1.17 g/cc | 1.09 - 1.17 g/cc | ASTM D792 |
| Melt Flow | 20 g/10 min @Load 5.00 kg, Temperature 250 °C |
20 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 82 | 82 | 30S reading; ASTM D2240 |
| Tensile Strength at Break | 13.0 MPa | 1890 psi | 50 mm/min; ISO 527 |
| 15.0 MPa | 2180 psi | Type I, 50 mm/min; ASTM D638 | |
| 20.0 MPa | 2900 psi | UL 1581 | |
| 21.0 MPa | 3050 psi | after 7days @113°C; UL 1581 | |
| Elongation at Break | 105 % | 105 % | 50 mm/min; ISO 527 |
| 160 % | 160 % | Type I, 50 mm/min; ASTM D638 | |
| 205 % | 205 % | after 7days @113°C; UL 1581 | |
| 260 % | 260 % | UL 1581 | |
| Flexural Modulus | 0.110 GPa | 16.0 ksi | 12.5 mm/min; ISO 178 |
| 0.130 GPa | 18.9 ksi | 12.5 mm/min, 100 mm span; ASTM D790 | |
| Heat Distortion | 15 % @Load 0.250 kg, Temperature 100 °C |
15 % @Load 0.551 lb, Temperature 212 °F |
UL 1581 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | UL temperature rating; UL 1581 |
| Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
| Oxygen Index | 25 % | 25 % | ISO 4589 |
| Glow Wire Test | 750 °C | 1380 °F | IEC 60695-2-13 |
| 850 °C @Thickness 3.00 mm |
1560 °F @Thickness 0.118 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.70e+15 ohm-cm | 2.70e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 20.0 kV/mm @Thickness 2.00 mm |
508 kV/in @Thickness 0.0787 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0040 @Frequency 1.00e+6 Hz |
0.0040 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Smoke Density on 0.5mm plaque, Flame, Ds, max | 127 | ASTM E 662 |
| Smoke Density on 0.5mm plaque, Non-flame, Ds, max | 133 | ASTM E 662 |
| VW-1 | Pass | UL 1581 |