Polymer Property : Modulus of Elasticity = 15.0 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	13.0 - 15.0 GPa	1890 - 2180 ksi	Injection; ISO 527
Raschig Group 2567 AMC Glass fiber-reinforced and inorganically filled polyester molding compound (UP) in various colors. Outstanding mechanical strength similar to BMC/SMC, very good electrical isolation properties and ..
Modulus of Elasticity	13.0 - 15.0 GPa	1890 - 2180 ksi	Injection; ISO 527
Raschig Group 2568 AMC Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for s..
Modulus of Elasticity	13.0 - 15.0 GPa	1890 - 2180 ksi	Injection; ISO 527
Raschig Group 2572 AMC Glass fiber reinforced Polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, good abrasion stability, high flame retardance in combin..
Modulus of Elasticity	0.824 - 15.0 GPa	119 - 2180 ksi	Average value: 9.44 GPa Grade Count:182
Overview of materials for Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled". Specific grades with glass content between 25..
Modulus of Elasticity	2.28 - 15.0 GPa	331 - 2180 ksi	Average value: 9.02 GPa Grade Count:8
Overview of materials for PET + PBT Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "PET + PBT Unreinforced". Each property range of values reported is minimum and maximum values of appropr..
Modulus of Elasticity	13.5 - 15.0 GPa @Temperature 70.0 - 70.0 °C	1960 - 2180 ksi @Temperature 158 - 158 °F	Average value: 10.1 GPa Grade Count:1
Overview of materials for Nylon 6, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. E..
Modulus of Elasticity	13.5 - 15.0 GPa @Time 180000 - 1.44e+6 sec	1960 - 2180 ksi @Time 50.0 - 400 hour	Average value: 10.1 GPa Grade Count:1
Overview of materials for Nylon 6, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. E..
Modulus of Elasticity	1.00 - 15.0 GPa	145 - 2180 ksi	Average value: 8.43 GPa Grade Count:471
Overview of materials for Nylon 66, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. ..
Modulus of Elasticity	1.00 - 15.0 GPa	145 - 2180 ksi	Average value: 7.98 GPa Grade Count:413
Overview of materials for Nylon 6, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E..
Modulus of Elasticity	0.210 - 15.0 GPa	30.5 - 2180 ksi	Average value: 2.32 GPa Grade Count:128
Overview of materials for Nylon 6, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Impact Grade". Each property range of values reported is minimum and maximum values of appropri..
Modulus of Elasticity	2.25 - 15.0 GPa	326 - 2180 ksi	Average value: 6.31 GPa Grade Count:143
Overview of materials for Polypropylene with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are i..