Material Notes:
Film made from LD 144.50 offers improved impact strength and heat sealability compared to homopolymer clarity film resins. Typically applications include food packaging, frozen food packaging, and textile goods packaging rack and counter bags.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.921 g/cc
0.0333 lb/in³
ExxonMobil Method
Vinyl Acetate Content 2.0 %
2.0 %
ExxonMobil Method
Melt Flow 2.0 g/10 min
2.0 g/10 min
ExxonMobil Method
Antiblock Level 3500 ppm
3500 ppm
Slip Level 725 ppm
725 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 9.10 MPa
1320 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 9.17 MPa
1330 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 160 %
160 %
ASTM D882
Film Elongation at Break, TD 550 %
550 %
ASTM D882
Film Elongation at Yield, MD 6.4 %
6.4 %
ASTM D882
Film Elongation at Yield, TD 5.5 %
5.5 %
ASTM D882
Elmendorf Tear Strength MD 310 g
310 g
ASTM D1922
Elmendorf Tear Strength TD 100 g
100 g
ASTM D1922
Dart Drop Test 140 g
0.309 lb
ASTM D1709
Film Tensile Strength at Break, MD 23.7 MPa
3440 psi
ASTM D882
Film Tensile Strength at Break, TD 20.7 MPa
3000 psi
ASTM D882
1% Secant Modulus, MD 172 MPa
24900 psi
ASTM D882
1% Secant Modulus, TD 208 MPa
30100 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 107 °C
224 °F
Peak Melting Temperature; ExxonMobil Method
Crystallization Temperature 94.0 °C
201 °F
ExxonMobil Method
Vicat Softening Point 90.0 °C
194 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 8.1 %
8.1 %
ASTM D1003
Gloss 63 %
63 %
45°; ASTM D2457
Descriptive Properties Value Comments
Features Thermal Stabilizer