Borealis HB306MO Polypropylene

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Borealis
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Borealis HB306MO Polypropylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

HB306MO is a low melt-flow-rate polypropylene homopolymer intended for compression molding of caps and closures. This grade is designed for the caps and closures market and therefore contains a lubricant for an optimum opening torque of the cap. This grade combines a good balance of stiffness and impact strength with good processability and melt stability. Additives provide anti-static protection. Applications: closures.Information provided by Borealis AG

Physical Properties	Metric	English	Comments
Density	0.910 g/cc	0.0329 lb/in³	ISO 1183
Linear Mold Shrinkage	0.010 - 0.020 cm/cm	0.010 - 0.020 in/in
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 230 °C	2.0 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	100	100	ISO 2039-2
Tensile Strength, Yield	39.0 MPa	5660 psi	ISO 527-2
Elongation at Yield	7.5 %	7.5 %	50mm/min; ISO 527-2
Tensile Modulus	1.90 GPa	276 ksi	1mm/min; ISO 527-2
Charpy Impact, Notched	0.550 J/cm² @Temperature 23.0 °C	2.62 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	88.0 °C	190 °F	ISO 75-2

Processing Properties	Metric	English	Comments
Melt Temperature	180 - 260 °C	356 - 500 °F