- Wellman EcoLon® 2000-BK1 37% Post Consumer Compound Nylon 66
Wellman EcoLon® 2000-BK1 37% Post Consumer Compound Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Wellman Engineering Resins |
| Trade Name | EcoLon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wellman EcoLon® 2000-BK1 37% Post Consumer Compound Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Post Consumer Compound Nylon 66Information provided by Wellman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183-87 |
| Filler Content | 37 % | 37 % | |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | ISO DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 105 MPa | 15200 psi | ISO 527-93 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-93 |
| Flexural Strength | 165 MPa | 23900 psi | ISO 178-93 |
| Flexural Modulus | 7.37 GPa | 1070 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 4.20 kJ/m² | 2.00 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-93 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 282 - 304 °C | 540 - 580 °F | |
| Middle Barrel Temperature | 282 - 293 °C | 540 - 560 °F | |
| Front Barrel Temperature | 271 - 282 °C | 520 - 540 °F | |
| Nozzle Temperature | 266 - 293 °C | 510 - 560 °F | |
| Melt Temperature | 282 - 304 °C | 540 - 580 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | Opened bags and gaylord boxes |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Opened bags and gaylord boxes |
| Moisture Content | 0.050 - 0.20 % | 0.050 - 0.20 % | During molding to prevent hydrolytic degradation |
| <= 0.20 % | <= 0.20 % | In shipping bags, ready to mold | |
| Injection Pressure | 34.5 - 138 MPa | 5000 - 20000 psi | |
| Back Pressure | 0.345 MPa | 50.0 psi | |
| Screw Speed | 30 - 120 rpm | 30 - 120 rpm |
Users viewing this material also viewed the following:
- Covestro Texin® DP7-3008 Thermoplastic Polyurethane, Polyester-based, Aliphatic (discontinued **)
- Ipiranga Petrochem PH 1710 Polypropylene
- H.C. Starck Grade KT 1 Crystalline Boron
- Henkel Turco Metal Glo #6 Jet Metal Brightener
- Solvay Luminostarâ„¢ Green A Phosphor
- SABIC Innovative Plastics NORYL LEN2211 PPE+HIPS (Asia Pacific)
- A. Schulman POLYFLAM™ FPP 1007E Talc Filled Homopolymer Polypropylene
- A. Schulman POLYFORT™ FPP 1285 Glass Fiber-Reinforced Copolymer Polypropylene
- ExxonMobil LLDPE LL 6101XR Linear Low Density Polyethylene Resin (European Grade)
- Chosun Refractories CT-140 Fireclay Castables
Copyright © lookpolymers.com All Rights Reserved