FKuR Kunststoff Bio-Flex® F 2201 CL Compostable PLA Blend

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer
Manufacturer FKuR Kunststoff GmbH
Trade Name Bio-Flex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF FKuR Kunststoff Bio-Flex® F 2201 CL Compostable PLA Blend.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The BIO-FLEX® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEX® does not contain any starch or starch derivatives. Bioplastics generally replace conventional materials such as low density polyethylene (LDPE), high density polythene (HDPE) as well as polystyrene (PS) and polypropylene (PP). For packaging applications these materials need to be converted into film which is as thin as possible while maintaining high tensile strength. Depending on the specific application, packaging films have to provide a high barrier against humidity, oxygen and aromas or alternatively provide adequate permeability (“breathability”).BIO-FLEX® F 2201 CL is predominantly composed of renewable resource raw materials. A film made from BIO-FLEX® F 2201 CL stands out due to its high transparency as well as its high flexibility and toughness. Due to the good interply strength of the layers this material is basically used in multilayer systems. Information Provided by FKuR Kunststoff GmbH
Physical Properties Metric English Comments
Density 1.25 g/cc
0.0452 lb/in³
ISO 1183
Melt Flow 8.0 - 10 g/10 min

@Load 2.16 kg,
Temperature 190 °C
8.0 - 10 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 27.0 MPa
3920 psi
ISO 527
Elongation at Yield >= 400 %
>= 400 %
ISO 527
Tensile Modulus 1.15 GPa
167 ksi
ISO 527
Flexural Yield Strength 28.0 MPa

@Strain 3.50 %
4060 psi

@Strain 3.50 %
Flexural Modulus 1.05 GPa
152 ksi
ISO 178
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179-1/1 eU
Charpy Impact, Notched 1.200 J/cm²

@Temperature 23.0 °C
5.710 ft-lb/in²

@Temperature 73.4 °F
ISO 179-1/1eA
Thermal Properties Metric English Comments
Melting Point 145 - 160 °C
293 - 320 °F
ISO 3146-C
Descriptive Properties Value Comments
Flexural strain at break (%) No break
ISO 178
Melt Volume Flow (cm3/10 min) 7-9.5
ISO 1133; 190°C, 2.16kg
Unnotched Charpy Impact Strength (kJ/m^2) No break
ISO 179-1/1 eU