- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- Samsung Cheil Industries Starex® WR-9330I Heat Resistant Grade ABS
Samsung Cheil Industries Starex® WR-9330I Heat Resistant Grade ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® WR-9330I Heat Resistant Grade ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D792 |
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 102 | 102 | ASTM D785 |
| Tensile Strength at Break | 43.4 MPa | 6300 psi | ASTM D638 |
| Elongation at Break | 66 % | 66 % | ASTM D638 |
| Flexural Strength | 64.8 MPa | 9400 psi | ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 3.52 J/cm | 6.60 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C @Thickness 6.35 mm |
201 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Vicat Softening Point | 101 °C | 214 °F | ISO R-306 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 200 - 220 °C | 392 - 428 °F | H1 |
| Middle Barrel Temperature | 220 - 240 °C | 428 - 464 °F | H2 |
| Front Barrel Temperature | 230 - 250 °C | 446 - 482 °F | H3 |
| Nozzle Temperature | 230 - 250 °C | 446 - 482 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 90.0 - 100 °C | 194 - 212 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 68.3 - 147 MPa | 9900 - 21300 psi | |
| Back Pressure | 0.979 - 1.96 MPa | 142 - 284 psi | |
| Screw Speed | 30 - 80 rpm | 30 - 80 rpm |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylon® N1000NL Nylon 6/6 (Cond) (discontinued **)
- Lucent Polymers CPP-0107 Polypropylene Homopolymer
- Inno-Comp INNOPOL® CS 1-1120 AN 20% Talc-Filled Polypropylene Homopolymer
- Solvay TECHNYL® A 548B2 V15 PA66, 15% glass fiber, DRY
- Techmer ES HiFill® PP 0142 B Polypropylene
- Wico Plast Wicolon 405 Polycarbonate
- A. Schulman POLYFORT™ FPP 1434 Couple Mica In Copolymer Polypropylene (25% Mineral Filled)
- Hexcel® HexForce™ 4450 Fiber Glass Fabric
- ACC QGel 315 QSI Quantum Silicones General Purpose Silicone Gel
Copyright © lookpolymers.com All Rights Reserved