- Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
- Lanxess Pocan® DP BF 4232 000000 PBT, 30% Glass Fiber
Lanxess Pocan® DP BF 4232 000000 PBT, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® DP BF 4232 000000 PBT, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT, 30% glass fibers, injection molding, flame retardant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in³ | ISO 1183 |
| Water Absorption | 0.40 % | 0.40 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0028 cm/cm | 0.0028 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0091 cm/cm | 0.0091 in/in | ISO 294-4, 2577 |
| Melt Flow | 23 g/10 min @Load 2.16 kg, Temperature 260 °C |
23 g/10 min @Load 4.76 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527-1/-2 |
| Elongation at Break | 2.4 % | 2.4 % | ISO 527-1/-2 |
| Tensile Modulus | 10.6 GPa | 1540 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Impact | 780 | 780 | Puncture maximum force (N); ISO 6603-2 |
| 720 @Temperature -30.0 °C |
720 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 1.90 J | 1.40 ft-lb | ISO 6603-2 |
| 1.70 J @Temperature -30.0 °C |
1.25 ft-lb @Temperature -22.0 °F |
ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 227 °C | 441 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 137 °C | 279 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
IEC 60695-11-10 |
| Oxygen Index | 32 % | 32 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+17 ohm | >= 1.00e+17 ohm | IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.1 @Frequency 100 Hz |
4.1 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 31.0 kV/mm | 787 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
IEC 60250 |
| 0.0165 @Frequency 1.00e+6 Hz |
0.0165 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Flame retardant | |
| Form | Pellets | |
| ISO Shortname | ISO 7792-PBT,GFHMR,09-110,GF30; ISO 1043-PBT GF FR(17) | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- RheTech Products T40P100-774UVA 40% Talc Reinforced Polypropylene, UV Stabilized, JA6A Black
- SABIC Innovative Plastics Cycoloy® XCM850 PC+ABS (Europe-Africa-Middle East)
- Resinlab® EP950NMF Gray Non-Metallic Filled Rubber Modified Epoxy
- ExxonMobil Escorene® LD-312 EVA Film Resin, High Impact (discontinued **)
- Haynes Hastelloy® C-4 alloy, all-weld metal, as welded, GTAW
- Lubrizol ESTANE® 58134 Ester Based Thermoplastic Polyurethane (European Grade)
- Addcomp PRIEX® Ionomer 30101 HDPE
- CENTROPLAST CENTROMID 12 soft Polyamide 12 soft
Copyright © lookpolymers.com All Rights Reserved