PolyOne Edgetek® SF-30GF/000 Polyphenylene Sulfide (PPS), Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® SF-30GF/000 Polyphenylene Sulfide (PPS), Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedUL 94 V0PolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.56 g/cc | 1.56 g/cc | ASTM D792 |
| Water Absorption | 0.040 % @Thickness 3.17 mm |
0.040 % @Thickness 0.125 in |
24 hr immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 138 MPa | 20000 psi | Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638 |
| Elongation at Break | 2.0 - 3.0 % | 2.0 - 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 13.1 GPa | 1900 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 200 MPa | 29000 psi | ASTM D790 |
| Flexural Modulus | 13.1 GPa | 1900 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 316 - 327 °C | 600 - 620 °F | Molding |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion 87564 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes
- Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Rod, 3 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter
- Sax Polymers SAXAMID 226F10 Nylon 6.6, 50% Glass Fiber
- CeramTec Alunit® Aluminum Nitride
- Unifrax FyreWrap® Elite™ 1.5 Duct Insulation Ventilation Air Duct (VAD) System
- Zotefoams Plastazote® LD24MC Low Density Polyethylene Foam, Medium Cell
- DuPont Performance Polymers Zytel® PLUS PLS95G50DH2 BK261 Nylon (Unverified Data**)
- ConocoPhillips Hydroclear® El Mar® Low Ash Heavy Duty SAE 30
- Asahi Kasei Thermylon® NSG-240A-2H 50% Ceramic and Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved