Unitika BV2120G30 PA66, 30% Glass Fiber Reinforced, Flame Retardant, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika BV2120G30 PA66, 30% Glass Fiber Reinforced, Flame Retardant, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.90 % | 0.90 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.20 mm |
0.0030 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 3.20 mm |
0.0070 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | ISO 2039 |
| Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527-1/-2 |
| Elongation at Break | 2.1 % | 2.1 % | ISO 527-1/-2 |
| Tensile Modulus | 12.2 GPa | 1770 ksi | ISO 527-1/-2 |
| Flexural Strength | 250 MPa | 36300 psi | ISO 178 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 256 °C | 493 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 28.0 kV/mm @Thickness 1.00 mm |
711 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 |
Users viewing this material also viewed the following:
- Eastman E6838-795F Polyethylene (discontinued **)
- DuPont Performance Polymers Zytel® 79G13HSL BK039 Nylon 66 (Unverified Data**)
- LG Chemical PB1302 PVC
- Johnson Matthey Mattibraze 35 Cadmium Containing Silver Brazing Alloy
- Karina E 06/923-IE MBU Blue Color Concentrate
- Solvay Specialty Polymers Diofan® P 520 Polyvinylidene Chloride (PVDC)
- Plenco 4466 Phenolic, Granular, Transfer Molded
- CMT Materials HYTAC® FLXT High Temperature, PTFE Impregnated Copolymer Syntactic
- Azoty Tarnow™ Alphalon™ 27C Nylon 6
- 3M FM0139 Indoor UL Recognized Clear Polyester Overlaminate Label Product
Copyright © lookpolymers.com All Rights Reserved