Toyobo NB-5620S Nylon/Olefin Alloy, 15% Mineral Reinforced (DAM)
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Toyobo |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo NB-5620S Nylon/Olefin Alloy, 15% Mineral Reinforced (DAM).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: 15% Mineral Reinforced, Light WeightInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D792 |
| Filler Content | 15 % | 15 % | |
| Water Absorption | 0.50 % | 0.50 % | 24 hrs at 23°C; ASTM D570 |
| 2.1 % | 2.1 % | 65% R.H. equilibrium; ASTM D570 | |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm @Thickness 1.00 mm |
0.0060 - 0.0080 in/in @Thickness 0.0394 in |
|
| 0.014 - 0.018 cm/cm @Thickness 3.00 mm |
0.014 - 0.018 in/in @Thickness 0.118 in |
||
| Melt Index of Compound | 8.0 g/10 min | 8.0 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ASTM D638 |
| 100 MPa @Temperature -40.0 °C |
14500 psi @Temperature -40.0 °F |
ASTM D638 | |
| Tensile Strength, Ultimate | 25.0 MPa @Temperature 80.0 °C |
3630 psi @Temperature 176 °F |
ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | ASTM D638 |
| Flexural Strength | 95.0 MPa | 13800 psi | ASTM D790 |
| 40.0 MPa @Temperature 80.0 °C |
5800 psi @Temperature 176 °F |
ASTM D790 | |
| 160 MPa @Temperature -40.0 °C |
23200 psi @Temperature -40.0 °F |
ASTM D790 | |
| Flexural Modulus | 3.70 GPa | 537 ksi | ASTM D790 |
| 2.80 GPa @Temperature 80.0 °C |
406 ksi @Temperature 176 °F |
ASTM D790 | |
| 6.20 GPa @Temperature -40.0 °C |
899 ksi @Temperature -40.0 °F |
ASTM D790 | |
| Izod Impact, Notched | 0.400 J/cm @Temperature -40.0 °C |
0.749 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| 0.540 J/cm @Temperature 23.0 °C |
1.01 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 25.0 kV/mm @Thickness 2.00 mm |
635 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 290 °C | 464 - 554 °F | |
| Mold Temperature | 50.0 - 120 °C | 122 - 248 °F | |
| Injection Pressure | 50.0 MPa | 7250 psi |
Users viewing this material also viewed the following:
- Radici Radilon® CS 35FL (cond.) Nylon 6/66
- PolyOne Edgetek® PK-30GF/000 Polyetheretherketone (PEEK)
- DSM Akulon® K-FHG12 (Dry) 60% Glass Reinforced Nylon 6 (North America) (discontinued **)
- Rostone Rosite® C200BS ESD SMC, Conductive Thermoset Polyester, 10% Glass Reinforced (discontinued **)
- LATI Laril 13-V1KC PPOm, Mineral Reinforced, Flame Retardant
- LATI Latamid SP2 H2 G/35 PA 6.12, 35% Glass Fiber Reinforced, Heat Stabilized
- Silberline Dedusted Flake Series DF-554 Aluminum Flake
- Total PPH 3462 Polypropylene, Extrusion Grade
- DuPont Performance Polymers Neoprene GRT M1 Polychloroprene Rubber
- ChevronTexaco Cygnus® Grease NLGI Grade 2
Copyright © lookpolymers.com All Rights Reserved