Polyram PlusTek PB300G2 Nylon 6 for Injection Molding, 10% Glass-Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PB300G2 Nylon 6 for Injection Molding, 10% Glass-Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% Glass-fiber reinforced, heat stabilized Nylon 6 for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 3.0 % | 3.0 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 9.5 % | 9.5 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | |
| Tensile Strength, Yield | 105 MPa | 15200 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 4.50 GPa | 653 ksi | ISO 527 |
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 |
| Flexural Modulus | 4.60 GPa | 667 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 218 °C | 424 °F | ISO 11357 |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous use |
| 200 °C | 392 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 80.0 kV/mm | 2030 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- Rotuba 860M Ethyl Cellulose
- Custom Resins Vexel™ E20GF45 , 45% Glass Reinforced PET (discontinued **)
- Haynes Hastelloy® W alloy as a weld filler, base metal Carbon steel 12.7 mm plate weldments
- Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes
- SABIC Innovative Plastics LNP LUBRICOMP NXCY620 PC+ABS
- Techmer ES Electrablend® PA6 CF30 TL10 30% Carbon Filled
- A. Schulman POLYFORT™ FPP 1908E Talc Filled Copolymer Polypropylene
- Total PPC 5752 Polypropylene, Heterophasic Copolymer
- 3M Scotch-Weld™ 4550 Industrial Adhesive
Copyright © lookpolymers.com All Rights Reserved