Teknor Apex Telcar® TL-1000-92 Thermoplastic Elastomer

Category	Polymer , Thermoplastic , Elastomer, TPE
Manufacturer	Teknor Apex Company
Trade Name	TELCAR®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Teknor Apex Telcar® TL-1000-92 Thermoplastic Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Automotive Specifications: Chrysler MS-DB590 CPN4660; Ford WSB-M4D734-AForms: Pellets Processing Method: Extrusion; Injection Molding Injection Notes: Injection Rate: Moderate-Fast Extrusion Notes: Screw Speed: 30 to 100 rpmInformation Provided by Teknor Apex

Physical Properties	Metric	English	Comments
Specific Gravity	0.920 g/cc	0.920 g/cc	ASTM D792
Linear Mold Shrinkage	0.011 cm/cm	0.011 in/in	ASTM D955
	0.013 cm/cm	0.013 in/in	ASTM D955
Melt Flow	2.00 g/10 min @Load 2.16 kg, Temperature 230 °C	2.00 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	95	95	15 seconds; ASTM D2240
Hardness, Shore D	42	42	10 seconds; ASTM D2240
Tensile Stress	8.41 MPa @Strain 100 %	1220 psi @Strain 100 %	2.0 in/min; ASTM D412
	8.55 MPa @Strain 300 %	1240 psi @Strain 300 %	2.0 in/min; ASTM D412
Tensile Strength, Yield	7.58 MPa	1100 psi	Type 1, 20 in/min; ASTM D638
	10.3 MPa	1490 psi	2.0 in/min; ASTM D638
Elongation at Break	140 %	140 %	Type 1, 20 in/min; ASTM D412
	550 %	550 %	2.0 in/min; ASTM D412
Elongation at Yield	16 %	16 %	Type 1, 20 in/min; ASTM D638
Flexural Modulus	0.290 GPa	42.1 ksi	ASTM D790
Poissons Ratio	0.337 @Temperature -35.0 °C	0.337 @Temperature -31.0 °F	ASTM D638
	0.363 @Temperature 85.0 °C	0.363 @Temperature 185 °F	ASTM D638
	0.419 @Temperature 23.0 °C	0.419 @Temperature 73.4 °F	ASTM D638
Izod Impact, Notched	NB @Temperature -40.0 °C	NB @Temperature -40.0 °F	ASTM D624
Gardner Impact	33.9 J @Temperature -30.0 °C	25.0 ft-lb @Temperature -22.0 °F	ASTM D3029
Tensile Impact Strength	470 kJ/m²	224 ft-lb/in²	ASTM D1822
Tear Strength	63.8 kN/m	364 pli	Die C; ASTM D1004

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	119 µm/m-°C @Temperature -30.0 - 30.0 °C	66.0 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM D696
CTE, linear, Transverse to Flow	117 µm/m-°C @Temperature -30.0 - 30.0 °C	65.0 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	62.8 °C	145 °F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	40.6 °C	105 °F	Unannealed; ASTM D648
Glass Transition Temp, Tg	-55.9 °C	-68.6 °F	DSC

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	171 - 193 °C	340 - 380 °F
Middle Barrel Temperature	177 - 199 °C	350 - 390 °F
Front Barrel Temperature	182 - 204 °C	360 - 400 °F
Nozzle Temperature	188 - 210 °C	370 - 410 °F
Zone 1	166 - 188 °C	330 - 370 °F
Zone 2	171 - 193 °C	340 - 380 °F
Zone 3	177 - 199 °C	350 - 390 °F
Zone 5	182 - 204 °C	360 - 400 °F
Die Temperature	190 - 210 °C	374 - 410 °F
Melt Temperature	188 - 210 °C	370 - 410 °F	Processing Temperature
Mold Temperature	25.0 - 65.6 °C	77.0 - 150 °F
Injection Pressure	1.38 - 6.89 MPa	200 - 1000 psi
Back Pressure	0.172 - 0.345 MPa	25.0 - 50.0 psi
Cushion	0.381 - 2.54 cm	0.150 - 1.00 in
Screw Speed	50 - 100 rpm	50 - 100 rpm