- Teijin Multilon TN-7500F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy
Teijin Multilon TN-7500F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate (PC) |
| Manufacturer | Teijin |
| Trade Name | Multilon |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teijin Multilon TN-7500F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. High stiffness and flowability realize the thin wall of large-scale business machine chassis.Information provided by Teijin Chemicals Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm @Thickness 4.00 mm |
0.0030 - 0.0050 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Thickness 4.00 mm |
0.0030 - 0.0050 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.0 MPa | 6960 psi | 50mm/min; ISO 527 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | 50mm/min; ISO 527 |
| Elongation at Break | 30 % | 30 % | 50mm/min; ISO 527 |
| Elongation at Yield | 2.0 % | 2.0 % | 50mm/min; ISO 527 |
| Flexural Strength | 96.0 MPa | 13900 psi | 2mm/min; ISO 178 |
| Flexural Modulus | 3.20 GPa | 464 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 60.0 µm/m-°C @Temperature 20.0 °C |
33.3 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75 |
| Flammability, UL94 | V-0 @Thickness 1.20 mm |
V-0 @Thickness 0.0472 in |
|
| 5VB @Thickness 1.80 mm |
5VB @Thickness 0.0709 in |
Users viewing this material also viewed the following:
- NYCOA 27/330KNF Glass Filled Nylon 6
- Nye Lubricants 113 (DMO) Delicate Machinery Oil
- SABIC Innovative Plastics Lexan® LS1 PC (Asia Pacific)
- Precision Polymer Engineering C60M Chloroprene Rubber
- Mar-Bal MB2000-5 Thermoset Polyester Composite Molding Compound
- Shinil Chemical SHINCON PES-CNT Magazine Rack
- Sichuan Deyang Haton® hs23310 Polyphenylene Sulfide Coating
- CLAL-MSX ARCAP Anticorrosion AP1 H12 1/2 hard, Rolled Copper Alloy
- 3M FM12E Indoor UL Recognized White Polyester Label Products
Copyright © lookpolymers.com All Rights Reserved