Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 96.0 MPa | 13900 psi | at <5%; ASTM D790 |
Ineos Nova PS 2520 Crystal Polystyrene
(discontinued **) Information provided by Nova ChemicalsINEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture between NOVA Chemicals and INEOS to include North American assets. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | at <5%; ASTM D790 |
Ineos Nova PS 2521 Crystal Polystyrene
(discontinued **) Information provided by Nova ChemicalsINEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture between NOVA Chemicals and INEOS to include North American assets. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | |
Lehmann & Voss LUVOCOM® 6-8548 Polyamide 12, with glass fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Suitable for discharging of statically generated electricity.Dynamic stressed parts.Low waterab.. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
Kolon KOCETAL® K500 Standard Grade Acetal Resin General injection molding grade. Easy flow grade for hard-to fill molds and mechanical thin-wall parts.Applications: General injection molding products.Information provided by API-Kolon. |
|||
Flexural Strength | 96.0 MPa @Temperature 22.0 °C |
13900 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
Menzolit Menzolit® BMC 2300 Unsaturated Polyester UP BMC 2300 is a special BMC with exceptional high fire retardancy. The glass content is set to a level that provides sufficient mouldability with high strength and stiffness properties. Fire retardanc.. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Lubricomp DX99854 PC (Asia Pacific) LNP* LUBRICOMP* DX99854 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated.This data was supplied by SABIC-I.. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | ISO 178 |
SABIC Innovative Plastics LNP Lubricomp EL004 PEI LNP* Lubricomp* EL004 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Americas.. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP HFG25Z PA 11 (Asia Pacific) LNP* Lubricomp* HFG25Z is a compound based on Nylon 11 resin containing Glass Fiber, Graphite Powder. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP IAL12 PA 6/12 (Asia Pacific) LNP* Lubricomp* IAL12 is a compound based on Nylon 6/12 resin containing PTFE, Aramid Fiber. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON DD0009E PC (Asia Pacific) LNP* Stat-kon* DD0009E is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Stat-kon DS0029 PC (Asia Pacific) LNP STAT-KON* DS0029 is a compound based on Polycarbonate resin containing Stainless Steel. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for t.. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON DX03571 PC LNP* STAT-KON* DX03571 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON DX03571 PC LNP* STAT-KON* DX03571 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-LOY 9X03508 PPO+PA66 (Asia Pacific) LNP* Stat-loy* 9X03508 is a compound based on PPO+PA66 resin containing Flame Retardant, Anti-Static. Added features of this material include: Antistat, Flame Retardant, High Impact. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP DZ004 PC (Asia Pacific) LNP* Thermocomp* DZ004 is a compound based on Polycarbonate resin containing Glass Fiber. Also known as Thermocomp DF-1004 M |
|||
Flexural Strength | 96.0 MPa | 13900 psi | 2mm/min; ISO 178 |
Teijin Multilon TN-7000F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. High stiffness realizes the thin wall of business machine chassis.Information provided by Teijin Chemicals Ltd. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | 2mm/min; ISO 178 |
Teijin Multilon TN-7500F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. High stiffness and flowability realize the thin wall of large-scale business machine chassis.Information provided by Tei.. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp PH0600A PA 6 LNP THERMOCOMP* PH0600A is a compound based on Nylon 6 resin. Added features of this material include: High Specific Gravity.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp PH0600A PA 6 (Asia Pacific) LNP* THERMOCOMP* PH0600A is a compound based on Nylon 6 resin. Added features of this material include: High Specific Gravity.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RZ006SXP PA 66 LNP* THERMOCOMP* RZ006SXP is a compound based on Nylon 66 resin containing 30% Milled Glass. Added feature of this material is: Heat Stabilized. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RI001 PA 66 LNP* LUBRICOMP* RI001 is a compound based on Nylon 66 resin containing 2% Silicone. Added feature of this grade is: Wear Resistant. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON DX05305C PC LNP* STAT-KON* DX05305C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding System. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-KON RD000 PA 66 LNP STAT-KON* RD000 is a compound based on Nylon 66 resin containing Carbon Powder. Added feature of this material is: Electrically Conductive. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Thermotuf VF002 PA 66 LNP THERMOTUF* VF002 is a compound based on Nylon resin containing Glass Fiber. Added features of this material include: High Impact.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | |
Zeon Chemicals Zeonex® 480R Cyclo-Olefin Polymer |
|||
Flexural Strength | 96.0 MPa | 13900 psi | 2 mm/min; ISO 178 |
Covestro Makrolon® 2408 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Medical devices - bioc.. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | 2 mm/min; ISO 178 |
Covestro Makrolon® 3100 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Hig.. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | 2 mm/min; ISO 178 |
Covestro Makrolon® ET2613 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Extrusion• Medium vi.. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP SF008 PA 12 (Asia Pacific) LNP* Thermocomp* SF008 is a compound based on Nylon 12 resin containing Glass Fiber. |
|||
Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
Plenco 4311 Phenolic, Granular, Transfer Molded PLENCO 04311 is a heat resistant, mineral filled phenolic molding compound offering excellent processability, mechanical strength, and improved cold powder pourability characteristics. UL recognized.. |