Suzhou Hipro Polymers Hiprolon® 400 MC HLS G30 Nylon, 30% glass fiber filled
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon |
| Manufacturer | Suzhou Hipro Polymers |
| Trade Name | Hiprolon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Suzhou Hipro Polymers Hiprolon® 400 MC HLS G30 Nylon, 30% glass fiber filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Hiprolon® 400 MC HLS G30 is a specialty long chain polyamide compound reinforced with 30% chopped glass fiber for injection molding. It contains some bio-renewable resources Features: high dimension stability, impact resistance, chemical resistance, superior cold impact resistance. Widely used for auto parts, electrical/machinery parts, thin-wall injection molding et al.Information provided by Suzhou Hipro Polymers Co. Ltd
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 |
| Water Absorption | 0.50 % | 0.50 % | ISO 62 |
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | normal; ISO 294-4,2577 |
| Linear Mold Shrinkage, Flow | 0.0065 cm/cm | 0.0065 in/in | ISO 294-4,2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 120 MPa | 17400 psi | ISO527-2/1A |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527-2/1A |
| Tensile Modulus | 6.50 GPa | 943 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 8.40 J/cm² @Temperature -30.0 °C |
40.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 8.60 J/cm² @Temperature 23.0 °C |
40.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 2.30 J/cm² @Temperature 23.0 °C |
10.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 189 °C | 372 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | ISO 75-1/2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | ISO 75-1/2 |
| Vicat Softening Point | 175 °C | 347 °F | ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
ISO1210 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
ISO1210 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ISO 60695 |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 280 °C | 446 - 536 °F | |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 70.0 - 130 MPa | 10200 - 18900 psi |
Users viewing this material also viewed the following:
- Overview of materials for Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler
- Greene Tweed Avalon® 57 PTFE, Thermoset Resin Filled
- LyondellBasell Astryn SZ021-2 Polypropylene Copolymer, 20% Talc
- Saint-Gobain Chemlam® 3320 Multi-plied, Flexible, Non-porous Fluoropolymer Laminated Composite
- Samsung Cheil Industries Infino® AR-9301 PA, Glass Filled General Purpose
- Wanhua Chemical Wanthane® WHT-8190 Polyether-Based TPU
- A. Schulman POLYFORT™ FPP 1606 Glass Filled Chemically Coupled Impact Copolymer Polypropylene
- Bulk Molding Compounds BMC A50-XHS Bulk molding compound
Copyright © lookpolymers.com All Rights Reserved