Styron INSPIREâ„¢ TF0808S(U) Polypropylene

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Styron
Trade Name	INSPIRE™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Styron INSPIREâ„¢ TF0808S(U) Polypropylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

TF0808S(U) is a talc filled PP exhibiting high impact resistance and a high stiffness. It is particularly well suited for low wall thickness bumper skins. INSPIRE TF0808S for painted parts INSPIRE TF0808SU for unpainted parts with a UV stabilization package Information provided by DowThe Inspire brand was spun off from Dow Chemical to Styron in 2010

Physical Properties	Metric	English	Comments
Density	0.930 g/cc	0.0336 lb/inÂ³	ISO 1183B
Filler Content	5 %	5 %	Talc
Linear Mold Shrinkage	0.0080 - 0.010 cm/cm	0.0080 - 0.010 in/in	ISO 294-4
Melt Flow	16.5 g/10 min @Load 2.16 kg, Temperature 230 Â°C	16.5 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	20.0 MPa	2900 psi	50mm/min; ISO 527
Elongation at Yield	>= 400 %	>= 400 %	ISO 527
Tensile Modulus	1.20 GPa	174 ksi	1 mm/min; ISO 527
Flexural Modulus	1.30 GPa	189 ksi	3 points and 2 mm/min; ISO 178
Izod Impact, Notched (ISO)	42.0 kJ/mÂ²	20.0 ft-lb/inÂ²	ISO 180/1A
	4.00 kJ/mÂ² @Temperature -40.0 Â°C	1.90 ft-lb/inÂ² @Temperature -40.0 Â°F	ISO 180/1A
Charpy Impact, Notched	4.50 J/cmÂ²	21.4 ft-lb/inÂ²	ISO 179-1/1eA
	0.400 J/cmÂ² @Temperature -40.0 Â°C	1.90 ft-lb/inÂ² @Temperature -40.0 Â°F	ISO 179-1/1eA

Thermal Properties	Metric	English	Comments
CTE, linear	63.0 Âµm/m-Â°C @Temperature -30.0 - 30.0 Â°C	35.0 Âµin/in-Â°F @Temperature -22.0 - 86.0 Â°F	DIN 53752
	93.0 Âµm/m-Â°C @Temperature 25.0 - 80.0 Â°C	51.7 Âµin/in-Â°F @Temperature 77.0 - 176 Â°F	DIN 53752
Deflection Temperature at 0.46 MPa (66 psi)	80.0 Â°C	176 Â°F	Unannealed; ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	50.0 Â°C	122 Â°F	Unannealed; ISO 75
Vicat Softening Point	125 Â°C	257 Â°F	9.8N / 120Â°C / h; ISO 306 A
Shrinkage	1.0 - 2.0 %	1.0 - 2.0 %	ISO 294-4

Processing Properties	Metric	English
Melt Temperature	190 - 260 Â°C	374 - 500 Â°F
Mold Temperature	20.0 - 60.0 Â°C	68.0 - 140 Â°F
Drying Temperature	80.0 Â°C	176 Â°F
Dry Time	2 hour	2 hour