Styron EMERGEâ„¢ 7570 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Styron
Trade Name EMERGE™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron EMERGEâ„¢ 7570 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Overview: EMERGEâ„¢ PC/ABS 7570 Advanced Resin is a high flow, ignition-resistant PC/ABS blend that contains now chlorinated or brominated additives. Its superior processing makes it ideal for injection molding of large, thin-wall, or intricate parts. EMERGE PC/ABS 7570 is suitable for use in a wide variety of applications in the Information Technology Equipment & Consumer Electronics industries. Applications:LCD TV EnclosuresCRT TV EnclosuresMonitor and PC EnclosuresInformation provided by Styron
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183/B
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ISO 294-4
Melt Flow 20 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 20 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ISO 1133
95 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 95 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 47.0 MPa

@Thickness 4.00 mm
 6820 psi

@Thickness 0.157 in
 Injection Molded; ISO 527-2/50
Tensile Strength, Yield 60.0 MPa

@Thickness 4.00 mm
 8700 psi

@Thickness 0.157 in
 Injection Molded; ISO 527-2/50
Elongation at Break 40 %

@Thickness 4.00 mm
 40 %

@Thickness 0.157 in
 Injection Molded; ISO 527-2/50
Elongation at Yield 4.0 %

@Thickness 4.00 mm
 4.0 %

@Thickness 0.157 in
 Injection Molded; ISO 527-2/50
Tensile Modulus 2.60 GPa

@Thickness 4.00 mm
 377 ksi

@Thickness 0.157 in
 Injection Molded; ISO 527-2/50
Flexural Strength 92.0 MPa

@Thickness 4.00 mm
 13300 psi

@Thickness 0.157 in
 2.0 mm/min, Injection Molded; ISO 178
Flexural Modulus 2.70 GPa

@Thickness 4.00 mm
 392 ksi

@Thickness 0.157 in
 2.0 mm/min, Injection Molded; ISO 178
Izod Impact, Notched (ISO) 12.0 kJ/m²

@Temperature 23.0 °C
 5.71 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/A
Charpy Impact, Notched 1.80 J/cm²

@Temperature 23.0 °C
 8.57 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
Hot Ball Pressure Test 95.0 °C
203 °F
IEC 60335-1
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C
194 °F
Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C
176 °F
Unannealed; ISO 75-2/A
Vicat Softening Point 98.0 °C
208 °F
ISO 306/B50
105 °C
221 °F
ISO 306/A120
Flammability, UL94 V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
 All Colors
V-0

@Thickness 2.50 mm
 V-0

@Thickness 0.0984 in
 Natural plus Color Concentrate
Glow Wire Test 800 °C

@Thickness 2.00 mm
 1470 °F

@Thickness 0.0787 in
 Ignition; IEC 60695-2-13
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 Index; IEC 60695-2-12
Processing Properties Metric English Comments
Melt Temperature 240 - 280 °C
464 - 536 °F
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Drying Temperature 80.0 - 90.0 °C
176 - 194 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour