Solvay Specialty Polymers Amodel® AFA-6133 V0 Z Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AFA-6133 V0 Z Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel AFA-6133 V0 Z is a 33% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin specifically formulated for connector applications requiring compatibility with both infrared and vapor phase soldering operations typically used by the electronics industry. Amodel AFA-6133 V0 Z offers high flow and short molding cycles, thereby enhancing molding productivity and lowering costs. - Black: AFA-6133 V0 Z BK 324Injection Notes: Injection Rate: 3 to 4 in/sec Holding Pressure: 50% of injection pressureData is presented for dry polymer unless noted as 'conditioned'.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.68 g/cc
0.0607 lb/in³
ISO 1183/A
Filler Content 33 %
33 %
Glass Fiber Reinforcement
Water Absorption 0.20 %

@Time 86400 sec
0.20 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength 166 MPa
24100 psi
Conditioned; ASTM D638
199 MPa
28900 psi
ASTM D638
Tensile Strength, Yield 63.4 MPa

@Temperature 175 °C
9200 psi

@Temperature 347 °F
Conditioned; ISO 527-2
63.4 MPa

@Temperature 175 °C
9200 psi

@Temperature 347 °F
ISO 527-2
75.2 MPa

@Temperature 150 °C
10900 psi

@Temperature 302 °F
Conditioned; ISO 527-2
75.2 MPa

@Temperature 150 °C
10900 psi

@Temperature 302 °F
ISO 527-2
114 MPa

@Temperature 100 °C
16500 psi

@Temperature 212 °F
Conditioned; ISO 527-2
114 MPa

@Temperature 100 °C
16500 psi

@Temperature 212 °F
ISO 527-2
186 MPa

@Temperature 23.0 °C
27000 psi

@Temperature 73.4 °F
ISO 527-2
186 MPa

@Temperature 23.0 °C
27000 psi

@Temperature 73.4 °F
Conditioned; ISO 527-2
Elongation at Break 1.7 %
1.7 %
Conditioned; ASTM D638
1.7 %
1.7 %
ASTM D638
1.6 %

@Temperature 23.0 °C
1.6 %

@Temperature 73.4 °F
ISO 527-2
1.6 %

@Temperature 23.0 °C
1.6 %

@Temperature 73.4 °F
Conditioned; ISO 527-2
2.4 %

@Temperature 100 °C
2.4 %

@Temperature 212 °F
Conditioned; ISO 527-2
2.4 %

@Temperature 100 °C
2.4 %

@Temperature 212 °F
ISO 527-2
4.9 %

@Temperature 175 °C
4.9 %

@Temperature 347 °F
ISO 527-2
4.9 %

@Temperature 175 °C
4.9 %

@Temperature 347 °F
Conditioned; ISO 527-2
5.1 %

@Temperature 150 °C
5.1 %

@Temperature 302 °F
ISO 527-2
5.1 %

@Temperature 150 °C
5.1 %

@Temperature 302 °F
Conditioned; ISO 527-2
Tensile Modulus 13.7 GPa
1990 ksi
Conditioned; ASTM D638
16.1 GPa
2340 ksi
ASTM D638
5.10 GPa

@Temperature 175 °C
740 ksi

@Temperature 347 °F
ISO 527-2
5.10 GPa

@Temperature 175 °C
740 ksi

@Temperature 347 °F
Conditioned; ISO 527-2
5.90 GPa

@Temperature 150 °C
856 ksi

@Temperature 302 °F
Conditioned; ISO 527-2
5.93 GPa

@Temperature 150 °C
860 ksi

@Temperature 302 °F
ISO 527-2
9.17 GPa

@Temperature 100 °C
1330 ksi

@Temperature 212 °F
ISO 527-2
9.20 GPa

@Temperature 100 °C
1330 ksi

@Temperature 212 °F
Conditioned; ISO 527-2
14.5 GPa

@Temperature 23.0 °C
2100 ksi

@Temperature 73.4 °F
Conditioned; ISO 527-2
14.5 GPa

@Temperature 23.0 °C
2100 ksi

@Temperature 73.4 °F
ISO 527-2
Flexural Strength 224 MPa
32500 psi
ASTM D790
229 MPa
33200 psi
Conditioned; ASTM D790
87.6 MPa

@Temperature 175 °C
12700 psi

@Temperature 347 °F
ISO 178
88.0 MPa

@Temperature 175 °C
12800 psi

@Temperature 347 °F
Conditioned; ISO 178
101 MPa

@Temperature 150 °C
14600 psi

@Temperature 302 °F
Conditioned; ISO 178
101 MPa

@Temperature 150 °C
14600 psi

@Temperature 302 °F
ISO 178
161 MPa

@Temperature 100 °C
23400 psi

@Temperature 212 °F
ISO 178
161 MPa

@Temperature 100 °C
23400 psi

@Temperature 212 °F
Conditioned; ISO 178
259 MPa

@Temperature 23.0 °C
37600 psi

@Temperature 73.4 °F
Conditioned; ISO 178
259 MPa

@Temperature 23.0 °C
37600 psi

@Temperature 73.4 °F
ISO 178
Flexural Modulus 13.1 GPa
1900 ksi
ASTM D790
13.3 GPa
1930 ksi
Conditioned; ASTM D790
4.60 GPa

@Temperature 175 °C
667 ksi

@Temperature 347 °F
Conditioned; ISO 178
4.62 GPa

@Temperature 175 °C
670 ksi

@Temperature 347 °F
ISO 178
4.96 GPa

@Temperature 150 °C
719 ksi

@Temperature 302 °F
ISO 178
5.00 GPa

@Temperature 150 °C
725 ksi

@Temperature 302 °F
Conditioned; ISO 178
8.07 GPa

@Temperature 100 °C
1170 ksi

@Temperature 212 °F
ISO 178
8.10 GPa

@Temperature 100 °C
1170 ksi

@Temperature 212 °F
Conditioned; ISO 178
12.6 GPa

@Temperature 23.0 °C
1830 ksi

@Temperature 73.4 °F
Conditioned; ISO 178
12.6 GPa

@Temperature 23.0 °C
1830 ksi

@Temperature 73.4 °F
ISO 178
Compressive Strength 145 MPa
21000 psi
ASTM D695
Shear Strength 62.1 MPa
9010 psi
Conditioned; ASTM D732
80.0 MPa
11600 psi
ASTM D732
Izod Impact, Notched 0.800 J/cm
1.50 ft-lb/in
Conditioned; ASTM D256
0.850 J/cm
1.59 ft-lb/in
ASTM D256
6.90 J/cm
12.9 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
Conditioned; ISO 180/1A
8.20 kJ/m²
3.90 ft-lb/in²
ISO 180/1A
Izod Impact, Unnotched (ISO) 44.0 kJ/m²

@Temperature 23.0 °C
20.9 ft-lb/in²

@Temperature 73.4 °F
Conditioned; ISO 180/1U
44.0 kJ/m²

@Temperature 23.0 °C
20.9 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched 4.60 J/cm²
21.9 ft-lb/in²
ISO 179/1eU
4.70 J/cm²
22.4 ft-lb/in²
Conditioned; ISO 179/1eU
Charpy Impact, Notched 1.40 J/cm²
6.66 ft-lb/in²
ISO 179/1eA
1.40 J/cm²
6.66 ft-lb/in²
Conditioned; ISO 179/2eA
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
ASTM D257
Dielectric Constant 4.1

@Frequency 1.00e+6 Hz
4.1

@Frequency 1.00e+6 Hz
ASTM D150