Styrolution TerluranÂ® GP-35 ABS

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
Manufacturer	Styrolution
Trade Name	Terluran®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Styrolution TerluranÂ® GP-35 ABS.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Terluran GP-35 is a very high flow grade of ABS for injection molding with good resistance to impact and heat deflection.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.

Physical Properties	Metric	English	Comments
Density	1.04 g/cc	0.0376 lb/inÂ³	ISO 1183
Water Absorption	0.95 %	0.95 %	ISO 62
Moisture Absorption at Equilibrium	0.24 %	0.24 %	23Â°C/50% R.H.; ISO 62
Linear Mold Shrinkage	0.0055 cm/cm	0.0055 in/in	ASTM Data; MD
Melt Flow	3.1 g/10 min @Load 5.00 kg, Temperature 200 Â°C	3.1 g/10 min @Load 11.0 lb, Temperature 392 Â°F	ASTM Test
	11 g/10 min @Load 3.80 kg, Temperature 230 Â°C	11 g/10 min @Load 8.38 lb, Temperature 446 Â°F	ASTM Test
	34 g/10 min @Load 10.0 kg, Temperature 220 Â°C	34 g/10 min @Load 22.0 lb, Temperature 428 Â°F	ISO 1133
	34 g/10 min @Load 10.0 kg, Temperature 220 Â°C	34 g/10 min @Load 22.0 lb, Temperature 428 Â°F	ASTM Test

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	102	102	ASTM Test
Tensile Strength, Yield	44.0 MPa	6380 psi	50mm/min; ISO 527
	45.0 MPa	6530 psi	2 in/min; ASTM Test
	19.0 MPa @Temperature 80.0 Â°C	2760 psi @Temperature 176 Â°F	ISO Data
	63.0 MPa @Temperature -40.0 Â°C	9140 psi @Temperature -40.0 Â°F	ISO Data
Elongation at Break	12 %	12 %	50mm/min, Nominal strain; ISO 527
Elongation at Yield	2.4 %	2.4 %	50mm/min; ISO 527
	2.4 %	2.4 %	2 in/min; ASTM Test
	2.5 % @Temperature 80.0 Â°C	2.5 % @Temperature 176 Â°F	ISO Data
	3.6 % @Temperature -40.0 Â°C	3.6 % @Temperature -40.0 Â°F	ISO Data
Tensile Modulus	2.30 GPa	334 ksi	1mm/min; ISO 527
	2.50 GPa	363 ksi	ASTM Test
Flexural Strength	65.0 MPa	9430 psi	ISO Data
	65.0 MPa	9430 psi	ASTM Test
Flexural Modulus	2.35 GPa	341 ksi	ASTM Test
Izod Impact, Notched	0.800 J/cm @Temperature -30.0 Â°C	1.50 ft-lb/in @Temperature -22.0 Â°F	ASTM Test
	0.850 J/cm @Temperature -18.0 Â°C	1.59 ft-lb/in @Temperature -0.400 Â°F	ASTM Test
	2.40 J/cm @Thickness 3.17 mm	4.50 ft-lb/in @Thickness 0.125 in	ASTM Test
Izod Impact, Notched (ISO)	22.0 kJ/mÂ²	10.5 ft-lb/inÂ²	ISO Test
Charpy Impact Unnotched	12.5 J/cmÂ²	59.5 ft-lb/inÂ²	ISO 179
	9.00 J/cmÂ² @Temperature -30.0 Â°C	42.8 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179
Charpy Impact, Notched	1.90 J/cmÂ²	9.04 ft-lb/inÂ²	ISO 179
	0.700 J/cmÂ² @Temperature -30.0 Â°C	3.33 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	95.0 Âµm/m-Â°C	52.8 Âµin/in-Â°F	ISO 11359
Deflection Temperature at 0.46 MPa (66 psi)	89.0 Â°C	192 Â°F	ASTM Test
	99.0 Â°C	210 Â°F	ISO 75
	101 Â°C	214 Â°F	annealed; ASTM Test
Deflection Temperature at 1.8 MPa (264 psi)	75.0 Â°C	167 Â°F	ASTM Test
	94.0 Â°C	201 Â°F	ISO 75
	97.0 Â°C	207 Â°F	annealed; ASTM Test
Vicat Softening Point	95.0 Â°C	203 Â°F	Rate "A" Loading 2 (50 degC/h 50N); ASTM Test
	95.0 Â°C	203 Â°F	(50 Â°C/h / 50N) - B/50; ISO 306
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in
	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093
Dielectric Strength	38.0 kV/mm	965 kV/in	IEC 60243-1

Processing Properties	Metric	English	Comments
Melt Temperature	250 Â°C	482 Â°F	Injection molding
Mold Temperature	83.0 Â°C	181 Â°F	Ejection temperature
Injection Velocity	60.0 mm/sec	2.36 in/sec	Injection molding

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	North America and Europe
FDA	Yes
Form	Pellets
Impact Modified	Yes
NSF Std. 14	Yes
NSF Std. 51	Yes
NSF Std. 61	Yes
Primary Processing Technique	Injection Molding
Processing	Injection Molding
Special characteristic	Platable
UL.UL-C	Yes
USP Class VI	No