Techmer ES Plaslube® J-1850/30/TF/15 PBT, 30% GFR, 15% PTFE
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Fiber + PTFE Filled |
| Manufacturer | Techmer ES |
| Trade Name | Plaslube® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Plaslube® J-1850/30/TF/15 PBT, 30% GFR, 15% PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in³ | ASTM D792 |
| Water Absorption | 1.16 % | 1.16 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 3.17 mm |
0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Break | 2.0 - 3.0 % | 2.0 - 3.0 % | ASTM D638 |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| Compressive Strength | 103 MPa | 15000 psi | ASTM D695 |
| Izod Impact, Notched | 0.694 J/cm @Thickness 3.17 mm |
1.30 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | |
| Coefficient of Friction, Static | 0.23 | 0.23 | |
| K (wear) Factor | 242 x 10-8 mm³/N-M | 120 x 10-10 in³-min/ft-lb-hr | Thrust washer at 2000 PV |
| Limiting Pressure Velocity | 0.701 MPa-m/sec | 20000 psi-ft/min | at 100 FPM, ambient temperature, thrust washer. |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 23.4 µm/m-°C @Temperature 20.0 °C |
13.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
Users viewing this material also viewed the following:
- Polimeri Europa Flexirene® MS 20 U Linear Low Density Polyethylene
- Solvay Specialty Polymers Solef® 32008 PVDF Copolymer (Unverified Data**)
- Solvay Specialty Polymers Solef® 6012 Polyvinylidene Fluoride (PVDF)
- SABIC Innovative Plastics Valox® 745 PBT (Europe-Africa-Middle East)
- Borealis Borclean™ HC314BF Polypropylene Homopolymer for Capacitor Film
- Teknor Apex Telcar® OBC 4945A Thermoplastic Elastomer
- Dow Corning SYL-OFF® 297 ANCHORAGE ADDITIVE
- EMS-Grivory Grivory® HT2C-3X black 9833 PA6T/66-CF30
- BASF 1,6-Dichlorohexane
Copyright © lookpolymers.com All Rights Reserved