- Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend, Glass Reinforced
- Styrolution Terblend® N NG-02 UV ABS / PA, 8% Glass filled
Styrolution Terblend® N NG-02 UV ABS / PA, 8% Glass filled
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend, Glass Reinforced |
| Manufacturer | Styrolution |
| Trade Name | Terblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Terblend® N NG-02 UV ABS / PA, 8% Glass filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Terblend N NG-02 UV is an 8% glass fiber reinforced (UV stabilized) ABS/PA blend with enhanced dimensional stability and rigidity.High dimensional stabilityEnhanced rigidityEnhanced softening temperatureGlass fiber reinforced (8%)Information provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.1 % @Temperature 23.0 °C |
1.1 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4 |
| Melt Flow | 30 g/10 min @Load 10.0 kg, Temperature 240 °C |
30 g/10 min @Load 22.0 lb, Temperature 464 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 95.0 MPa | 13800 psi | ISO 2039-1 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 3.30 GPa | 479 ksi | ISO 527 |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
| Flexural Modulus | 2.85 GPa | 413 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact Unnotched | 2.50 J/cm² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 60.0 µm/m-°C | 33.3 µin/in-°F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75 |
| Vicat Softening Point | 108 °C @Load 5.10 kg |
226 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| 170 °C @Load 1.02 kg |
338 °F @Load 2.25 lb |
50°C/h; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.013 @Frequency 1.00e+6 Hz |
0.013 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | ISO 294 |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | ISO 294 |
Users viewing this material also viewed the following:
- PolyOne OnFlex™ S HS 70A-3E2543 Thermoplastic Elastomer (TPE)
- PolyMirae Moplen EP648N Injection Molding Grade Polypropylene
- PolyOne Dynalloy™ OBC 8100-N75 Thermoplastic Elastomer (TPE)
- Karina TR-500D10/1-YV White PVC Compound
- Kraton® G1657 + PA-6,6 blend (8/12/80)
- Tra-Con Tra-Bond F156 Optically Opaque Epoxy Adhesive
- A. Schulman SCHULAMID® 66 MV3 Unreinforced Nylon 6/6
- Arlon CLTE-XT High Precision Ceramic PTFE
- 3M Novec™ Contact Cleaner Plus
Copyright © lookpolymers.com All Rights Reserved