LG Chemical LUMILOY GP2200 Injection Molding Grade, General Purpose 20% Glass Reinforced PPE
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 20% Glass Filled |
| Manufacturer | LG Chemical |
| Trade Name | LUMILOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMILOY GP2200 Injection Molding Grade, General Purpose 20% Glass Reinforced PPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
NSF Certified for KA02 and E2035. Noted for High Flow, High Impact Strength, and Hydrolytic Stability. Uses include electric/electronic parts and water pump Housing or impellers and other parts with water contact.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 |
| Melt Flow | 9.5 g/10 min @Load 5.00 kg, Temperature 280 °C |
9.5 g/10 min @Load 11.0 lb, Temperature 536 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 95.1 MPa @Thickness 3.20 mm |
13800 psi @Thickness 0.126 in |
ASTM D638 |
| Elongation at Break | 7.0 % @Thickness 3.17 mm |
7.0 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Strength | 137 MPa @Thickness 3.20 mm |
19900 psi @Thickness 0.126 in |
ASTM D790 |
| Flexural Modulus | 4.90 GPa @Thickness 3.20 mm |
711 ksi @Thickness 0.126 in |
ASTM D790 |
| Izod Impact, Notched | 1.03 J/cm @Thickness 3.20 mm |
1.93 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Izod Impact, Unnotched | 4.51 J/cm @Thickness 3.20 mm |
8.45 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 300 °C | 500 - 572 °F | |
| Middle Barrel Temperature | 270 - 310 °C | 518 - 590 °F | |
| Front Barrel Temperature | 270 - 310 °C | 518 - 590 °F | |
| Nozzle Temperature | 270 - 310 °C | 518 - 590 °F | |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |
| Drying Temperature | 80 - 100 °C | 180 - 212 °F | |
| Dry Time | 4 - 5 hour | 4 - 5 hour | |
| Moisture Content | >= 0.03 % | >= 0.03 % |
Users viewing this material also viewed the following:
- Nitriflex N-7420P NBR / PVC
- SSAB Tunnplat Docol® 800 DL High-strength Steel
- Dyna-Purge® B Purging Compound
- SABIC Innovative Plastics NORYL WCD841U PPE-TPE (Asia Pacific)
- Plenco 00732 Melamine-Phenolic, Granular, Injection Molded
- Tisan TISOPLEN® Flame Retardant (V0). Heat Stabilized, Copolymer Polypropylene
- Master Bond Supreme 11 High Peel and Shear Strength Epoxy Adhesive
- ChevronTexaco 4R Unconventional Base Oil
- Alliance Polymers Viprene™ G50A-32U-BLK Thermoplastic Vulcanizate Elastomer
- 3M 7027 Screen Printable Polyester Performance Label Products
Copyright © lookpolymers.com All Rights Reserved