Styrolution Luran® S 778 UV Colored ASA

Category Polymer , Thermoplastic , ASA Polymer
Manufacturer Styrolution
Trade Name Luran®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styrolution Luran® S 778 UV Colored ASA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection molding grade with enhanced toughness and resistance to heat distortion. Especially suitable for exterior automotive components (e.g. radiator grills, rear end appliqué panels and mirror housings).Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ISO 1183
Water Absorption 1.65 %
1.65 %
Equilibrium; ISO 62
0.45 %

@Time 86400 sec
0.45 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 0.35 %
0.35 %
23°C/50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
Melt Flow 5.35 g/10 min

@Load 10.0 kg,
Temperature 220 °C
5.35 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 85.0 MPa

@Load 36.5 kg,
Time 30.0 sec
12300 psi

@Load 80.5 lb,
Time 0.00833 hour
ISO 2039-1
Tensile Strength, Yield 54.0 MPa
7830 psi
50 mm/min; ISO 527-1/-2
Elongation at Break 8.0 %
8.0 %
Nominal, 50 mm/min; ISO 527-1/-2
Elongation at Yield 3.4 %
3.4 %
50 mm/min; ISO 527-1/-2
Tensile Modulus 2.50 GPa
363 ksi
ISO 527-1/-2
Flexural Strength 80.0 MPa
11600 psi
ISO 178
Izod Impact, Notched 2.50 J/cm
4.68 ft-lb/in
ASTM D256
Charpy Impact Unnotched 9.00 J/cm²

@Temperature -30.0 °C
42.8 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
25.0 J/cm²

@Temperature 23.0 °C
119 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.400 J/cm²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
1.50 J/cm²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Tensile Creep Modulus, 1000 hours 1250 MPa

@Strain <=0.500 %
181000 psi

@Strain <=0.500 %
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 - 110 µm/m-°C

@Temperature 23.0 - 80.0 °C
44.4 - 61.1 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-1/-2
Thermal Conductivity 0.170 W/m-K
1.18 BTU-in/hr-ft²-°F
DIN 52612-1
Maximum Service Temperature, Air 90.0 °C
194 °F
Deflection Temperature at 0.46 MPa (66 psi) 106 °C
223 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 103 °C
217 °F
ISO 75-1/-2
Vicat Softening Point 104 °C
219 °F
VST/B/50; ISO 306
113 °C
235 °F
VST/A/50; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
IEC 60695-11-10
HB

@Diameter 4.00 mm
HB

@Diameter 0.157 in
IEC 60707
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 3.5

@Frequency 1.00e+6 Hz
3.5

@Frequency 1.00e+6 Hz
IEC 60250
3.9

@Frequency 100 Hz
3.9

@Frequency 100 Hz
IEC 60250
Dielectric Strength 35.0 kV/mm
889 kV/in
K20/P20; IEC 60243-1
Dissipation Factor 0.0090

@Frequency 100 Hz
0.0090

@Frequency 100 Hz
IEC 60250
0.033

@Frequency 1.00e+6 Hz
0.033

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
Test Liquid A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 240 - 280 °C
464 - 536 °F
Injection
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Injection
Drying Temperature 80.0 °C
176 °F
Pre-drying
Dry Time 2 - 4 hour
2 - 4 hour
Pre-drying
Descriptive Properties Value Comments
Color Gray 35968
Gray 36565
Gray 36899
Gray 36934
Gray 37096
Natural
White 36508
Commercial Status Europe
Primary Processing Technique Injection Molding