Radici Radilon® S LHS (dry) Nylon 6

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer	Radici Group Plastics
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Radici Radilon® S LHS (dry) Nylon 6.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group.

Physical Properties	Metric	English	Comments
Specific Gravity	1.14 g/cc	1.14 g/cc
Water Absorption	10.2 %	10.2 %
Moisture Absorption at Equilibrium	3.1 %	3.1 %
Viscosity Measurement	125	125	cm³/g Viscosity Number

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	80.0 MPa	11600 psi
Elongation at Break	25 %	25 %	Nominal
Elongation at Yield	4.0 %	4.0 %
Tensile Modulus	3.30 GPa	479 ksi
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F
Charpy Impact, Notched	0.430 J/cm² @Temperature -30.0 °C	2.05 ft-lb/in² @Temperature -22.0 °F
	0.700 J/cm² @Temperature 23.0 °C	3.33 ft-lb/in² @Temperature 73.4 °F

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F
Deflection Temperature at 0.46 MPa (66 psi)	170 °C	338 °F
Deflection Temperature at 1.8 MPa (264 psi)	60.0 °C	140 °F
Vicat Softening Point	190 °C @Load 5.10 kg	374 °F @Load 11.2 lb	50°C/h
Flammability, UL94	V-2 @Thickness 1.60 mm	V-2 @Thickness 0.0630 in
	V-2 @Thickness 0.800 mm	V-2 @Thickness 0.0315 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+11 ohm-cm	>= 1.00e+11 ohm-cm