SABIC Innovative Plastics ULTEM 1010X PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM 1010X PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Enhanced flow Polyetherimide (Tg 217C) with low ionic contamination of less than 0.1 ppm each of leachable chloride and sulphates. ECO Conforming. Factory Mutual FM4910 compliant in recognized colors.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Water Absorption | 0.25 % @Time 86400 sec |
0.25 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 17.8 g/10 min @Load 6.60 kg, Temperature 337 °C |
17.8 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 109 | 109 | ASTM D785 |
| Tensile Strength, Yield | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 60 % | 60 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.58 GPa | 519 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 165 MPa | 23900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 3.51 GPa | 509 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.35 J/cm | 25.01 ft-lb/in | ASTM D4812 |
| Taber Abrasion, mg/1000 Cycles | 10 | 10 | CS-17, 1 kg; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 55.8 µm/m-°C @Temperature -20.0 - 150 °C |
31.0 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 |
| Thermal Conductivity | 0.220 W/m-K | 1.53 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 207 °C @Thickness 6.40 mm |
405 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C @Thickness 6.40 mm |
388 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 218 °C | 424 °F | Rate B/50; ASTM D1525 |
| Glass Transition Temp, Tg | 217 °C | 423 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.15 @Frequency 1000 Hz |
3.15 @Frequency 1000 Hz |
ASTM D150 |
| Dielectric Strength | 27.9 kV/mm @Thickness 1.60 mm |
709 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 |
| 32.6 kV/mm @Thickness 1.60 mm |
828 kV/in @Thickness 0.0630 in |
in air; ASTM D149 | |
| Dissipation Factor | 0.0013 @Frequency 1000 Hz |
0.0013 @Frequency 1000 Hz |
ASTM D150 |
| 0.0025 @Frequency 2.45e+9 Hz |
0.0025 @Frequency 2.45e+9 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXD9945A PC (Asia Pacific)
- Materion BrushBronze® 95510 (AMS 4880) Centrifugal Cast 0.250" - 1.0"
- SABIC Innovative Plastics NORYL N1150 PPE+PS
- A. Schulman POLYBATCH™ Popular Choice White HS80660 Concentrate Based In Polystyrene
- Dow Corning JCR 6101 UP
- Elektro-Isola G-Etronax M Melamine, Glass Fabric Reinforcement, White, Tubes
- 3M FM692 Indoor UL Recognized Computer Imprintable Clear Polyester Label Product
- Solvay Specialty Polymers Amodel® AT-6130 HS Polyphthalamide (PPA) (Unverified Data**)
- SABIC Innovative Plastics SABIC STAMAX 60YK270 PP
- Braskem TX7003 LDPE Blown Film Extrusion Polyethylene
Copyright © lookpolymers.com All Rights Reserved