A. Schulman FORMION™ FI 105E Non-Reinforced, Extrusion Grade Sodium Ionomer

Category	Polymer , Thermoplastic , Ionomer , Ionomer, Molded
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	A. Schulman FORMION™ FI 105E Non-Reinforced, Extrusion Grade Sodium Ionomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

DescriptionFormion® FI 1051E is a non-reinforced, transparent, extrusion grade Sodium Ionomer. It has been formulated for high durability, cut and puncture resistance, and low temperature ductility. ApplicationFormion® FI 105E is targeted for exterior or interior appearance or packaging applications in film, blow molding, thermoforming or extrusion applications, which may require high or low gloss, excellent colorability or transparency.Information provided by A. Schulman.

Physical Properties	Metric	English	Comments
Specific Gravity	0.940 g/cc	0.940 g/cc	ISO 1183/1
Linear Mold Shrinkage	0.0060 - 0.018 cm/cm @Thickness 3.20 mm	0.0060 - 0.018 in/in @Thickness 0.126 in	72 hr; ISO 294
Melt Index of Compound	1.0 g/10 min @Load 2.16 kg, Temperature 190 °C	1.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	60	60	15 sec delay; ISO 868
Tensile Strength, Ultimate	21.0 MPa	3050 psi	at max load; ISO 527
Tensile Strength, Yield	21.0 MPa	3050 psi	ISO 527
Elongation at Break	275 %	275 %	ISO 527
Flexural Modulus	0.360 GPa	52.2 ksi	Tangent; ISO 178
Izod Impact, Notched (ISO)	NB	NB	ISO 180

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	39.0 °C @Thickness 3.20 mm	102 °F @Thickness 0.126 in	ISO 75

Optical Properties	Metric	English	Comments
Transmission, Visible	90 %	90 %	transparent; thickness not quantified