Solvay Technyl® C 216 Nylon 6, 30% Glass Fiber, EH0
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® C 216 Nylon 6, 30% Glass Fiber, EH0.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide PA6, reinforced with 30% of glass fiber, for injection molding.It has good mechanical properties. It is used in all sectors of industry, offering an excellent combination between thermal and mechanical properties. It is used in the automotive industry and electrical sectors. This product is available in colors on request.Glow wire test thick. 1,6 mm, IEC 695-2-1, is 650°C. Glow wire test thick. 1,6 mm:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183-A |
| Water Absorption | 0.95 % | 0.95 % | 24 hours in water at 23°C; ISO 62. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 190 MPa | 27600 psi | ISO 527 |
| Elongation at Break | 3.8 % | 3.8 % | ISO 527 |
| Tensile Modulus | 9.60 GPa | 1390 ksi | ISO 527 |
| Flexural Yield Strength | 280 MPa | 40600 psi | ISO 178 |
| Flexural Modulus | 9.50 GPa | 1380 ksi | ISO 178 |
| Izod Impact Resistance | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 10.0 J/cm² | 47.6 ft-lb/in² | ISO 179/1EA-1993 |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179/1EA-1993 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 32.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
17.8 µin/in-°F @Temperature 73.4 - 185 °F |
ASTM E831 |
| Melting Point | 222 °C | 432 °F | ISO 3146-C |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-2 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
ISO 1210/UL 94 |
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
ISO 1210/UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 93 |
| Dielectric Constant | 3.8 @Frequency 1e+6 Hz |
3.8 @Frequency 1e+6 Hz |
IEC 250 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 225 - 230 °C | 437 - 446 °F | |
| Middle Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |
| Front Barrel Temperature | 240 - 250 °C | 464 - 482 °F |
Users viewing this material also viewed the following:
- Proto3000 Accura® 50 Plastic Stereolithography (SLA) Prototyping Polymer
- Quadrant EPP Ertacetal® C POM-C, extruded (ISO Data)
- Hyosung Topilene HJ340 PP
- H.C. Starck Amperit® 568.005 Tungsten Carbide-Nickel 92-8 - Nickel SF RC 60 65-35
- SABIC Innovative Plastics LNP Stat-loy K3000 Acetal Copoly
- Zircar Ceramics NKO Castertip
- Crucible Steel CPM® Rex® T15(HS), AISI T15 High Speed Steel Rex® T15(HS)
- Fainplast Compounds GA 76/R Flexible PVC, Flame Retardant Sheathing
- Huntsman PE1061 Film Extrusion Polyethylene (discontinued **)
- Plaskolite West Optix® CA - 75 UVT General Purpose Acrylic Resin
Copyright © lookpolymers.com All Rights Reserved