DSM Novamid® ST120 NAT PA6-I
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Novamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Novamid® ST120 NAT PA6-I.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Impact Modified, Injection Molding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 2.80 % | 2.80 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm | 0.020 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | dry; ISO 527-1/-2 |
| Elongation at Break | 30 % | 30 % | dry; ISO 527-1/-2 |
| >= 50 % | >= 50 % | cond; ISO 527-1/-2 | |
| Elongation at Yield | 4.2 % | 4.2 % | dry; ISO 527-1/-2 |
| Tensile Modulus | 1.90 GPa | 276 ksi | dry; ISO 527-1/-2 |
| Flexural Strength | 60.0 MPa | 8700 psi | dry; ISO 178 |
| Flexural Modulus | 1.70 GPa | 247 ksi | dry; ISO 178 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond; ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| Charpy Impact, Notched | 4.20 J/cm² @Temperature 23.0 °C |
20.0 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | dry; ISO 11359-1/-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 87.0 °C | 189 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
dry; IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 9.00e+14 ohm-cm | 9.00e+14 ohm-cm | dry; IEC 60093 |
| Surface Resistance | 3.00e+13 ohm | 3.00e+13 ohm | cond; IEC 60093 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
dry; IEC 60250 |
| 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
dry; IEC 60250 | |
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | dry; IEC 60243-1 |
| Dissipation Factor | 0.010 @Frequency 100 Hz |
0.010 @Frequency 100 Hz |
dry; IEC 60250 |
| 0.018 @Frequency 1.00e+6 Hz |
0.018 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | dry; IEC 60112 |
Users viewing this material also viewed the following:
- PolyChem Alloy PolyStat 3K1
- DuPont Nucrel® 2806 Ethylene-Acrylic Acid Copolymer Resin (discontinued **)
- Overview of materials for Nylon 610, Carbon Fiber Filled
- Michelman® Michem® Emulsion 98040M1 Nonionic Fischer Tropsch wax emulsion
- Microplasmic Anodizing [Ceramic Coating] for Aluminum, Magnesium, Titanium, Zirconium & Composites
- Teknor Apex Monprene® MP-1538A Thermoplastic Elastomer
- Polyplastics Duracon® SF-15 Acetal Co-polymer (POM), High impact, Flexible
- Parker Chomerics CHO-SHIELD® 1091 Adhesion Promoter for Conductive Polyurethane Coatings
Copyright © lookpolymers.com All Rights Reserved