A. Schulman POLYFLAM™ RABS 930-01
| Category | Polymer , Thermoplastic |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYFLAM™ RABS 930-01.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0051 cm/cm | 0.0051 in/in | ASTM D955 |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 31.9 MPa | 4630 psi | ASTM D638 |
| Elongation at Yield | 18 % | 18 % | ASTM D638 |
| Flexural Strength | 50.0 MPa | 7250 psi | ASTM D790 |
| Flexural Modulus | 1.938 GPa | 281.1 ksi | ASTM D790 |
| Izod Impact, Notched | 1.15 J/cm | 2.15 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 89.4 °C | 193 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.3 °C | 168 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
Users viewing this material also viewed the following:
- Radici Radilon® A HS (cond.) Nylon 66
- Chevron Phillips K-Resin® CK02 Styrene-Butadiene Copolymer, Blow Molding Grade (discontinued **)
- Struktol VP 3643 Optimized elastomer-modified epoxy prepolymer
- Teknor Apex Chemlon® 109 Nylon 66, Impact Grade
- Stratasys® ABS-M30
- DuPont Vamac® GLS Sample Compound
- A. Schulman POLYFORT™ FPP 1237 CaCO3 filled homopolymer polypropylene
- Eastman Tenite Butyrate 285A2R30016 Natural, Trsp Cellulose Acetate Butyrate
- ChevronTexaco Havoline® MERCON® V Automatic Transmission Fluid
- A. Schulman POLYFLAM™ RPP 1058 General Purpose Homopolymer Polypropylene (30% Fiberglass)
Copyright © lookpolymers.com All Rights Reserved