- Solvay Technyl® A20V25 25% Glass Filled, V-0 Nylon 66
Solvay Technyl® A20V25 25% Glass Filled, V-0 Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® A20V25 25% Glass Filled, V-0 Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| Water Absorption | 0.75 % | 0.75 % | 24 Hr.; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength at Break | 135 MPa | 19600 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 8.62 GPa | 1250 ksi | ASTM D638 |
| Flexural Strength | 205 MPa | 29700 psi | ASTM D790 |
| Flexural Modulus | 7.52 GPa | 1090 ksi | ASTM D790 |
| Izod Impact, Notched | 0.731 J/cm | 1.37 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 255 °C | 491 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
|
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 270 - 275 °C | 518 - 527 °F | |
| Middle Barrel Temperature | 275 - 280 °C | 527 - 536 °F | Compression Zone |
| Front Barrel Temperature | 279 - 285 °C | 535 - 545 °F | |
| Melt Temperature | 270 - 280 °C | 518 - 536 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Surface |
| Drying Temperature | 80.0 °C | 176 °F | Dehumidifying Dryer |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | |
| Back Pressure | 0.138 - 0.345 MPa | 20.0 - 50.0 psi | |
| Fill Speed | 200 - 300 mm/sec | 7.87 - 11.8 in/sec | Peripheral Screw Speed |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed (cm3/sec) | 80 - 120 cm3/sec |
Users viewing this material also viewed the following:
- PolyMirae Moplen HP601N Injection Molding Grade Polypropylene
- ExxonMobil Santoprene® 8221-60 Thermoplastic Rubber (discontinued **)
- Mearthane Durethaneâ„¢ S DS-680A Solid Polyurethane Elastomer
- Lucent Polymers G6-15 Nylon 6, 15% Glass Fiber Reinforced
- Lucent Polymers GPB-130 Polybutylene Terephthalate, 30% Glass Fiber Reinforced
- Techmer ES HiFill® PP 0225 B Polypropylene
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 5.0 PHR MBTS
- Lubrizol Estane® S375D Thermoplastic Polyurethane
- Polyram RamSter PF392G6 PBT, 30% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved