Solvay Technyl® A 216 V30 Nylon 66, 30% Glass Fiber, EH50
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® A 216 V30 Nylon 66, 30% Glass Fiber, EH50.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide PA66, reinforced with 30% of glass fiber, for injection molding.Technyl A 216 V30 is used in all sectors of industry, offering an excellent combination between thermal and mechanical properties. This grade is used in automotive industry, manufacture of components of electrical tools, and transport and building.This product is available in natural, black and in a wide range of standard colors.Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183-A |
| Water Absorption | 0.80 % | 0.80 % | (Beginning Dry) 24 hours in water 23°C. ISO 62 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | RHODIA-EP |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | RHODIA-EP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 135 MPa | 19600 psi | ISO 527 |
| Tensile Strength, Yield | 135 MPa | 19600 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 7.50 GPa | 1090 ksi | ISO 527 |
| Flexural Yield Strength | 176 MPa | 25500 psi | ISO 178 |
| Flexural Modulus | 5.90 GPa | 856 ksi | ISO 178 |
| Izod Impact Resistance | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 9.50 J/cm² | 45.2 ft-lb/in² | ISO 179/EU-1993 |
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 179/1EA-1993 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | ISO 3146-C |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 2.00e+13 ohm-cm | 2.00e+13 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 93 |
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz |
4.0 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 243-1 |
| Dissipation Factor | 0.11 @Frequency 1e+6 Hz |
0.11 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Nozzle Temperature | 271 - 279 °C | 520 - 535 °F | |
| Melt Temperature | 270 - 300 °C | 518 - 572 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | Surface |
| Drying Temperature | 80.0 °C | 176 °F | Dehumidifying Dryer |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | |
| Back Pressure | 0.138 - 0.345 MPa | 20.0 - 50.0 psi | |
| Fill Speed | 200 - 300 mm/sec | 7.87 - 11.8 in/sec | Peripheral Screw Speed |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed (cm3/sec) | 120 - 170 cm3/sec |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HP1R PC (Asia Pacific)
- Eastman 1925F Polyethylene Film (discontinued **)
- Hong Kun Group UV 360 UV Absorber
- SABIC Innovative Plastics LNP Thermocomp 5X06476 FP-V (PVDF)
- Saint-Gobain CHR® 6004 Glass-Foil Backing Silicone Adhesive Pressure Sensitive Tape
- Westlake Plastics Tempalux® Polyetherimide
- A. Schulman POLYFORT™ FPP 3452 Mineral Filled Copolymer Polypropylene
- ExxonMobil Label-Lyte™ 47LTL247 OPP Film
- BASF Propylamine
Copyright © lookpolymers.com All Rights Reserved