PolyOne OnFlex™ HT 50A-3S2099 Thermoplastic Elastomer (TPE)

Category	Polymer , Thermoplastic , Elastomer, TPE
Manufacturer	PolyOne Corporation
Trade Name	OnFlex™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne OnFlex™ HT 50A-3S2099 Thermoplastic Elastomer (TPE).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

OnFlex™ HT thermoplastic elastomer compounds are based on hydrogenated styrenic block copolymers. This range of compounds is specially formulated to deliver very good compression set performance at elevated temperatures and a high heat resistance. Furthermore, OnFlex™ S HT compounds are in compliance with EN 681-2 and offer excellent mechanical properties, a wide hardness range and good processability.Properties are measured using injection molded plaques.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Density	1.00 g/cc	0.0361 lb/in³	ISO 1183

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	60	60	IRHD; ISO 48
	50 @Temperature 23.0 °C	50 @Temperature 73.4 °F	Injection Molded; DIN 53505
Tensile Strength at Break	5.20 MPa @Thickness 2.00 mm, Temperature 23.0 °C	754 psi @Thickness 0.0787 in, Temperature 73.4 °F	200 mm/min Flow; DIN 53504
	9.40 MPa @Thickness 2.00 mm, Temperature 23.0 °C	1360 psi @Thickness 0.0787 in, Temperature 73.4 °F	200 mm/min Across Flow; DIN 53504
Tensile Stress	1.10 MPa @Strain 100 %	160 psi @Strain 100 %	Across Flow; ISO 37
	1.70 MPa @Strain 100 %	247 psi @Strain 100 %	Flow; ISO 37
	1.90 MPa @Strain 300 %	276 psi @Strain 300 %	Across Flow; ISO 37
	2.90 MPa @Strain 300 %	421 psi @Strain 300 %	Flow; ISO 37
Elongation at Break	560 % @Thickness 2.00 mm, Temperature 23.0 °C	560 % @Thickness 0.0787 in, Temperature 73.4 °F	200 mm/min Flow; DIN 53504
	800 % @Thickness 2.00 mm, Temperature 23.0 °C	800 % @Thickness 0.0787 in, Temperature 73.4 °F	200 mm/min Across Flow; DIN 53504
Compression Set	20 % @Temperature 23.0 °C, Time 259000 sec	20 % @Temperature 73.4 °F, Time 72.0 hour	ISO 815
	27 % @Temperature 70.0 °C, Time 79200 sec	27 % @Temperature 158 °F, Time 22.0 hour	ISO 815
	36 % @Temperature -10.0 °C, Time 79200 sec	36 % @Temperature 14.0 °F, Time 22.0 hour	ISO 815
	42 % @Temperature 100 °C, Time 79200 sec	42 % @Temperature 212 °F, Time 22.0 hour	ISO 815
	46 % @Temperature 125 °C, Time 79200 sec	46 % @Temperature 257 °F, Time 22.0 hour	ISO 815
	50 % @Temperature -10.0 °C, Time 259000 sec	50 % @Temperature 14.0 °F, Time 72.0 hour	ISO 815
	69 % @Temperature 150 °C, Time 79200 sec	69 % @Temperature 302 °F, Time 22.0 hour	ISO 815

Processing Properties	Metric	English	Comments
Melt Temperature	180 - 220 °C	356 - 428 °F
Mold Temperature	30.0 - 60.0 °C	86.0 - 140 °F

Descriptive Properties	Value	Comments
Change in Shore Hardness in Air	3 Shore A	DIN 53505; Shore A, 70°C, 168 hr
Change in Tensile Strain at Break in Air	3%	DIN 53504; 70°C, 168 hr, 2.00 mm
Change in Tensile Strength in Air	-3%	DIN 53504; 70°C, 168 hr, 2.00 mm
Change in Volume	-0.6%	ISO 1817; 70°C, 168 hr, in Water
	16%	ISO 1817; 70°C, 72 hr, in ASTM #1 Oil
Features	High Heat Resistance
	Low Compression Set
	Ozone Resistant
Forms	Pellets
Generic Material	TPE
Generic Material Type	Styrenic Thermoplastic Elastomer (TES)
Generic Name	Thermoplastic Elastomer (TPE)
Injection Rate	Fast
Manufacturer / Supplier	GLS Thermoplastic Elastomers
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
RoHS Compliance	RoHS Compliant
Stress Relaxation	13%	ISO 3384; 23°C; 168hrs, 25% compression, Method A
	24%	ISO 3384; 23°C; 100d, 25% compression, Method A
Uses	Pipe Seals