EPICHEM Epilac ABS Acrylonitrile Butadiene Styrene
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | EPICHEM srl |
| Trade Name | Epilac |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EPICHEM Epilac ABS Acrylonitrile Butadiene Styrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792, ISO 1183 |
| Water Absorption | 0.30 % @Temperature 23.0 °C |
0.30 % @Temperature 73.4 °F |
24h; ASTM D570, ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Index of Compound | 14 - 20 g/10 min @Load 10.0 kg, Temperature 220 °C |
14 - 20 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238, ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 107 | 107 | ASTM D785, ISO 2039/2 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ASTM D638, ISO R527 |
| Elongation at Break | 25 % | 25 % | ASTM D638, ISO R527 |
| Flexural Strength | 65.0 MPa | 9430 psi | ASTM D790, ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790, ISO 178 |
| Izod Impact, Notched | 0.600 J/cm @Thickness 3.20 mm, Temperature -30.0 °C |
1.12 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F |
ASTM D256, ISO 180/4a |
| 1.10 J/cm @Thickness 3.20 mm, Temperature 0.000 °C |
2.06 ft-lb/in @Thickness 0.126 in, Temperature 32.0 °F |
ASTM D256, ISO 180/4a | |
| 1.60 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
3.00 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256, ISO 180/4a |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | >= 80.0 °C | >= 176 °F | BS 3456, IEC 335 |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ASTM D648, ISO 75 |
| Vicat Softening Point | 97.0 °C @Load 5.00 kg |
207 °F @Load 11.0 lb |
120°C/min; ASTM D1525/B, ISO 306/B |
| 106 °C @Load 0.999 kg |
223 °F @Load 2.20 lb |
120°C/min; ASTM D1525/A, ISO 306/A | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Glow Wire Test | 650 °C @Thickness 3.20 mm |
1200 °F @Thickness 0.126 in |
VDE 0471/P2-4, IEC 695 |
| 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
VDE 0471/P2-4, IEC 695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257, IEC 93 |
| Dielectric Constant | 3.2 @Frequency 1000 Hz |
3.2 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | ASTM D149, IEC 243 |
| Dissipation Factor | 0.015 @Frequency 1000 Hz |
0.015 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | VDE 0303-P1, IEC 112 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics GELOY CR7020 ASA (Asia Pacific)
- Lehmann & Voss LUVOCOM® 1/GF/20/TF/10/SI/2/BK Polyamide 66, with glass fiber, PTFE, lubricant modified
- SABIC Innovative Plastics NORYL WCA871A PPE (Europe-Africa-Middle East)
- Techmer ES HiFill® PA6 GF60 HS L 60% Glass Filled
- SABIC Innovative Plastics NORYL PPX PPX7110 PPE+PP (Asia Pacific)
- Eastman Eastar AN004 Natural PCTA Copolyester
- Alliance N-40SH Neodymium Iron Boron Magnetic Material
- A. Schulman POLYBATCH™ Orange 1046E Concentrate Based In Polyethylene
- Resinlab® SEC1222 Silver Filled Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved