Solvay Technyl® A 216 V30 Nylon 66, 30% Glass Fiber, EH0
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® A 216 V30 Nylon 66, 30% Glass Fiber, EH0.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide PA66, reinforced with 30% of glass fiber, for injection molding.Technyl A 216 V30 is used in all sectors of industry, offering an excellent combination between thermal and mechanical properties. This grade is used in automotive industry, manufacture of components of electrical tools, and transport and building.This product is available in natural, black and in a wide range of standard colors. Glow wire test thick. 1,6 mm, IEC 695-2-1, is 650°C. Glow wire test thick. 3,2 mm, IEC 695-2-1, is 750°C. Glow wire test thick. 1,6 mm: no flame, IEC 695-2-1, is 650°C.Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183-A |
| Water Absorption | 0.80 % | 0.80 % | 24 hours in water at 23°C; ISO 62. |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | RHODIA-EP |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | RHODIA-EP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 190 MPa | 27600 psi | ISO 527 |
| Tensile Strength, Yield | 190 MPa | 27600 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527 |
| Flexural Yield Strength | 260 MPa | 37700 psi | ISO 178 |
| Flexural Modulus | 8.40 GPa | 1220 ksi | ISO 178 |
| Izod Impact Resistance | 1.10 J/cm² | 5.24 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | ISO 179/EU-1993 |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179/1EA-1993 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
13.9 µin/in-°F @Temperature 73.4 - 185 °F |
ASTM E831 |
| Melting Point | 263 °C | 505 °F | ISO 3146-C |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
ISO 1210/UL 94 |
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Surface Resistance | 6.00e+14 ohm | 6.00e+14 ohm | IEC 93 |
| Dielectric Constant | 3.75 @Frequency 1e+6 Hz |
3.75 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 243-1 |
| Dissipation Factor | 0.010 @Frequency 1e+6 Hz |
0.010 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Nozzle Temperature | 271 - 279 °C | 520 - 535 °F | |
| Melt Temperature | 270 - 300 °C | 518 - 572 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | Surface |
| Drying Temperature | 80.0 °C | 176 °F | Dehumidifying Dryer |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | |
| Back Pressure | 0.138 - 0.345 MPa | 20.0 - 50.0 psi | |
| Fill Speed | 200 - 300 mm/sec | 7.87 - 11.8 in/sec | Peripheral Screw Speed |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed | 120 - 170 cm3/sec |
Users viewing this material also viewed the following:
- PTS Trilac® FR3800 Flame Retardant ABS Resin, RoHS Compliant
- Solvay Specialty Polymers Amodel® A-1145 HS Polyphthalamide (PPA) (Unverified Data**)
- Overview of materials for Polycarbonate/ABS Alloy, Glass Fiber Filled
- ExxonMobil Escorene® LD-129 MDPE Cast Overwrap Film Resin (discontinued **)
- SGL Carbon Group SIGRAFIL C® C25 P350 PUT Pelletized Carbon Fiber, Polyurethane Sizing
- SABIC Innovative Plastics Xenoy® 5720U PBT+PC (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP DB008ERP PC
- Polyram PlusTek PA7001G7BK11 Nylon 66, 35% Glass Fiber Reinforced, Heat and UV Stabilized, Hydrolysis Resistant
- DSM Akulon® Ultraflow™ K-FHG6 Nylon 6-30% Glass Reinforced (European Grade) (Cond)
- SABIC Innovative Plastics Ultem ATX103R PEI+PCE (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved