PolyOne Bergamid™ B70 G30 grey VN7445CF Polyamide 6 (Nylon 6)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Bergamid™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Bergamid™ B70 G30 grey VN7445CF Polyamide 6 (Nylon 6).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ±0.03; DIN 53479 |
| Linear Mold Shrinkage | 0.0010 - 0.0060 cm/cm @Thickness 4.00 mm, Temperature 23.0 °C |
0.0010 - 0.0060 in/in @Thickness 0.157 in, Temperature 73.4 °F |
Flow Bergmann Method; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 120 MPa @Thickness 4.00 mm, Temperature 23.0 °C |
17400 psi @Thickness 0.157 in, Temperature 73.4 °F |
5.0 mm/min; ISO 527 |
| Elongation at Break | 2.0 % @Thickness 4.00 mm, Temperature 23.0 °C |
2.0 % @Thickness 0.157 in, Temperature 73.4 °F |
5.0 mm/min; ISO 527 |
| Tensile Modulus | 7.80 GPa @Thickness 4.00 mm, Temperature 23.0 °C |
1130 ksi @Thickness 0.157 in, Temperature 73.4 °F |
Injection Molded; ISO 527-2/1 |
| Flexural Strength | 175 MPa @Temperature 23.0 °C |
25400 psi @Temperature 73.4 °F |
ISO 178 |
| Flexural Modulus | 7.00 GPa @Temperature 23.0 °C |
1020 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact Unnotched | 4.80 J/cm² @Temperature 23.0 °C |
22.8 ft-lb/in² @Temperature 73.4 °F |
Injection Molded; ISO 179 |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
Injection Molded; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 8.0 MPa | 210 °C | 410 °F | Unannealed; ISO 75-2/C |
| Flammability, UL94 | HB @Thickness 0.800 - 3.00 mm |
HB @Thickness 0.0315 - 0.118 in |
ALL; Internal Method |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | |
| Mold Temperature | 65.0 - 85.0 °C | 149 - 185 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Good Dimensional Stability | |
| Good Flow | ||
| Good Stiffness | ||
| Filler / Reinforcement | Glass Fiber Reinforcement, 30% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | Nylon 6 | |
| Generic Name | Polyamide 6 (Nylon 6) | |
| Processing Method | Injection Molding | |
| Regional Availability | Europe | |
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- Noble Polymers Regis™ 250107 Thermoplastic Olefin (TPO)
- Kingfa PA6-G30 N101 30% Glass Fiber Reinforced PA6 (general purpose)
- Shinkong Synthetic Fibers Shinite® N601G30 Nylon 66, 30% Glass Filled
- Sawbones Solid Rigid Polyurethane Foam 10 pcf Density
- A. Schulman INVISION™ FX-9090UE Soft Touch Polyolefin Thermoplastic
- DSM Akulon® S223-HG6 Nylon 66-30% Glass Reinforced (European and Asian Grade) (Cond)
- Eagle Brass 102 OF COPPER (Non-Certified), Annealed
- Ascend Performance Materials Vydyne® 47H Nylon 66, Impact Modified, DAM
- ExxonMobil Santoprene® 201-67W171 Thermoplastic Vulcanizate (discontinued **)
- ChevronTexaco AFP White Oil
Copyright © lookpolymers.com All Rights Reserved