Solvay Technyl® A 205F Nylon 66, EH50
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® A 205F Nylon 66, EH50.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unreinforced polyamide 66, high fluidity, fast cycling grade, for injection molding.Technyl A 205F offers two main advantages: excellent filling qualities and UL 94 V2 under 0.4 mm. It is particularly suitable for the molding of long parts with thin wall sections, such as: cable tie, fasteners, and connectors.This product is available in natural, black and in colors on request.Glow wire test thick. 1,6 mm, IEC 695-2-1, is 960°C.Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183-A |
| Water Absorption | 1.2 % | 1.2 % | (Beginning Dry) 24 hours in water 23°C. ISO 62 |
| Linear Mold Shrinkage | 0.019 cm/cm | 0.019 in/in | RHODIA-EP |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in | RHODIA-EP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ISO 527 |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527 |
| Elongation at Break | 200 % | 200 % | ISO 527 |
| Elongation at Yield | 10 % | 10 % | ISO 527 |
| Tensile Modulus | 1.60 GPa | 232 ksi | ISO 527 |
| Flexural Yield Strength | 50.0 MPa | 7250 psi | ISO 178 |
| Flexural Modulus | 1.30 GPa | 189 ksi | ISO 178 |
| Izod Impact Resistance | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | NB | NB | ISO 179/EU-1993 |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1EA-1993 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | ISO 3146-C |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 93 |
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz |
3.2 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 26.0 kV/mm | 660 kV/in | IEC 243-1 |
| Dissipation Factor | 0.080 @Frequency 1e+6 Hz |
0.080 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 270 - 275 °C | 518 - 527 °F | |
| Middle Barrel Temperature | 280 - 285 °C | 536 - 545 °F | |
| Front Barrel Temperature | 285 - 290 °C | 545 - 554 °F |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-BOND 1029 Conductive Adhesive
- Teknor Apex APEX® 3800-90 Polyvinyl Chloride, Flexible
- SABIC Innovative Plastics LNP THERMOCOMP RX98372H PA 66
- Sumitomo Chemical Sumipex® LG Acrylic Resin, High Flow
- A. Schulman POLYPUR™ FPU 1152C Thermoplastic Polyurethane
- Wellman Wellamid® 22L-NBK1 Engineering Grade Nylon 66
- ConocoPhillips Hydroclear Diamond Class® 68 AW Turbine Oil
- Eurotec® Tecomid® NA40 NL IL PA6.6, impact modified, natural
- Arlon R33920W028 0.028" (0.711 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved