- Solvay TECHNYLSTARâ„¢ S 218 MT PA6, 40% mineral filled, DRY
Solvay TECHNYLSTARâ„¢ S 218 MT PA6, 40% mineral filled, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Mineral Filled |
| Manufacturer | Solvay |
| Trade Name | TECHNYLSTAR™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYLSTARâ„¢ S 218 MT PA6, 40% mineral filled, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: TechnylStar Polyamide, 40% mineral filled, heat stabilized, for injection molding. Characterized by a high fluidity of the melt.Available in: Asia Pacific and North AmericaProduct Applications: This grade has good mechanical properties. It is suitable for automotive industry and specially designed for electroplating. This product is available in naturalInformation provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183/A |
| Water Absorption | 0.72 % @Temperature 23.0 °C, Time 86400 sec |
0.72 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0097 cm/cm | 0.0097 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0074 cm/cm | 0.0074 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0076 cm/cm | 0.0076 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527 Type 1A |
| Elongation at Break | 8.0 % | 8.0 % | ISO 527 Type 1A |
| Tensile Modulus | 5.80 GPa | 841 ksi | ISO 527 Type 1A |
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 |
| Flexural Modulus | 5.50 GPa | 798 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.50 kJ/m² | 2.62 ft-lb/in² | ISO 180/1eA |
| Izod Impact, Unnotched (ISO) | 85.0 kJ/m² | 40.4 ft-lb/in² | ISO 180/1eU |
| Charpy Impact Unnotched | 7.50 J/cm² | 35.7 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
1210 |
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 | |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
1210 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 220 - 230 °C | 428 - 446 °F | |
| Front Barrel Temperature | 245 - 250 °C | 473 - 482 °F | |
| Mold Temperature | 80.0 °C | 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 240-250°C |
Users viewing this material also viewed the following:
- Global GX-92 PPO Polyphenylene Ether + PS
- HP Alloys Alloy X, 30% Cold Worked
- A. Schulman POLYBATCH™ Green 3012E Concentrate Based In Polyethylene
- Hexcel® HexWeb® CR-PAA™ 3/8-5052-0.0015 Phosphoric Acid Anodized Aluminum Honeycomb
- DuPont™ Kapton® HPP-ST Polyimide Film
- Fainplast Compounds GS 55/T Flexible PVC, Injection Molding for Footwear
- ConocoPhillips Hydroclear® 32 Ultra-clean multi-purpose R&O Oil
- Fainplast Compounds PH 66/A Flexible PVC, Transparent Extrusion
- Arlon Thermabond® R36211A008 0.008" (0.203 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Aclo Accutech ABS ABS831G20L Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved