Aclo Accutech Polypropylene Homopolymer HP0336G40CL Glass Reinforced Coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Glass Fiber Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0336G40CL Glass Reinforced Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | MD; ASTM D955 |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
| Ash | 40 % | 40 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength at Break | 81.98 MPa | 11890 psi | ASTM D638 |
| Tensile Strength, Yield | 81.98 MPa | 11890 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 4.599 GPa | 667.1 ksi | ASTM D638 |
| Flexural Strength | 117.0 MPa | 16970 psi | ASTM D790 |
| Flexural Modulus | 7.2988 GPa | 1058.6 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm | 1.30 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PP 1450R (Z30S) Propylene Homopolymer
- SABIC Innovative Plastics Lexan® XHT2146 PC Copolymer
- PolyOne Edgetek® AS-15GF/000 Acrylonitrile Butadiene Styrene (ABS), Glass Filled (discontinued **)
- H.C. Starck HPM 1700 Tungsten High Density Composite
- Karina 600D48/1-C-IS Black PVC Compound
- A. Schulman SCHULADUR® B GF15 15% Glass Fiber Reinforced PET
- Covestro Makrolon® GF8002* Polycarbonate, 15% Glass Filled
- Dow Nordel® NDR 4820P EPDM Hydrocarbon Rubber
- Arkema Group Pebax® MV 1041 SN 01 Polyether Block Amide (PEBA) (Conditioned)
- 3M 9505 Adhesive Transfer Tapes with Adhesive 220
Copyright © lookpolymers.com All Rights Reserved