Beijing Chemical Industry KAIFA® 301-G30RF PBT Resin
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant |
| Manufacturer | Beijing Chemical Industry Research Institute (Group) |
| Trade Name | KAIFA® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Beijing Chemical Industry KAIFA® 301-G30RF PBT Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass fiber reinforced, flame retardant, good toughness, low bleedingInformation provided by Beijing Chemical Industry Research Institute (Group)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ASTM D792 |
| Water Absorption | 0.040 % | 0.040 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 MPa | 17400 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Strength | 180 MPa | 26100 psi | ASTM D790 |
| Flexural Modulus | 6.50 GPa | 943 ksi | ASTM D790 |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | ISO179 |
| Charpy Impact, Notched | 1.80 J/cm² | 8.57 ft-lb/in² | ISO179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 43.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
23.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz |
3.2 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 22.0 kV/mm @Thickness 2.00 mm |
559 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.017 @Frequency 1e+6 Hz |
0.017 @Frequency 1e+6 Hz |
ASTM D150 |
| Comparative Tracking Index | 250 V @Thickness 3.20 mm |
250 V @Thickness 0.126 in |
ASTM D3638 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 225 - 255 °C | 437 - 491 °F | |
| Nozzle Temperature | 245 °C | 473 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi | |
| Back Pressure | 8.00 - 18.0 MPa | 1160 - 2610 psi | |
| Screw Speed | <= 100 rpm | <= 100 rpm |
Users viewing this material also viewed the following:
- DuPont Elvax® 462 Ethylene-Vinyl Acetate Copolymer Resin (discontinued **)
- Firestone CLM200-001 Nylon 6
- Michelman® Licomer® W 315 FP Anionic / Nonionic polyethylene emulsion
- Latrobe DuraTechâ„¢ T15 Powder Metal High Speed Steel (ASTM T15)
- Saint-Gobain COHRlastic® 3016 Low Temperature Flexibility Silicone Coated Fabric
- Esstech X-167-0340 Glass Ionomer Cement Liquid
- Aclo Accutech Polypropylene Copolymer CP0436T30L1 Talc Reinforced
- Buckeye Polymers BP ABS 4233 B ABS
- DuPont Performance Polymers Zytel® RS 30G30HSL BK038A Nylon 610 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved