Solvay TECHNYL® PSB 286 PA6, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® PSB 286 PA6, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Unreinforced polyamide PA6, with very good lubrication, standard for fast injection cycles, for injection molding.Available in: North AmericaProduct Applications: This grade has high fluidity and good mould release. It is particularly suitable for the production of technical moldings with fast injection cycles.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183/A |
| Water Absorption | 1.3 % @Temperature 23.0 °C, Time 86400 sec |
1.3 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm | 0.012 in/in | |
| Linear Mold Shrinkage, Transverse | 0.016 cm/cm | 0.016 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527 Type 1A |
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | ISO 527 type 1 A |
| Elongation at Break | 65 % | 65 % | ISO 527 Type 1A |
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527 Type 1A |
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| Flexural Modulus | 2.80 GPa | 406 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 222 °C | 432 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75/Af |
| Flammability, UL94 | V-2 @Thickness 0.800 mm |
V-2 @Thickness 0.0315 in |
1210 |
| V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
1210 | |
| V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
1210 | |
| Glow Wire Test | 700 °C @Thickness 0.800 mm |
1290 °F @Thickness 0.0315 in |
ISO 60695-2-12 |
| 700 °C @Thickness 1.60 mm |
1290 °F @Thickness 0.0630 in |
ISO 60695-2-12 | |
| 750 °C @Thickness 3.20 mm |
1380 °F @Thickness 0.126 in |
ISO 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 3.4 | 3.4 | IEC 60250 |
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 225 - 230 °C | 437 - 446 °F | |
| Front Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |
| Mold Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 230-235°C |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable EHA70L Polyvinyl Chloride, Flexible (PVC, Flexible)
- S&E Specialty Polymers GTPO8290-GT7 PVC
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.0 mm thick sheet
- GrafTech GRAFOIL® TG-411 Non-Standard Fluid Sealing Graphite, High Temperature
- Borealis BC142MO Polypropylene Copolymer
- Cancarb Thermax® Powder N908 Stainless Medium Carbon Black
- 3M Cushion-Mount™ 1815M Plus Plate Mounting Tape
- Armstrong A-40 Epoxy Adhesive
- 3M Scotch-Weld™ 2216 B/A Tan NS Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved