Kuraray Genestarâ„¢ GT2330 Nylon, 33% Glass Filled
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Kuraray Company |
| Trade Name | Genestar™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kuraray Genestarâ„¢ GT2330 Nylon, 33% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Toughness V-0 Grade. It is well suited for components requiring a high strength in pin fitting process, due to high ductility properties.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.58 g/cc | 1.58 g/cc | |
| Water Absorption | 1.0 % | 1.0 % | |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 320 °C |
15 g/10 min @Load 4.76 lb, Temperature 608 °F |
ASTM D1238 |
| Spiral Flow | 4.50 cm @Load 750 kg, Temperature 320 °C |
1.77 in @Load 1650 lb, Temperature 608 °F |
0.5mm diameter |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 60.0 MPa | 8700 psi | Weld; ASTM D638 |
| 190 MPa | 27600 psi | ASTM D638 | |
| Elongation at Yield | 0.80 % | 0.80 % | Weld; ASTM D638 |
| 4.3 % | 4.3 % | ASTM D638 | |
| Flexural Strength | 240 MPa | 34800 psi | ASTM D790 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ASTM D790 |
| Izod Impact, Notched | 1.00 J/cm | 1.87 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 306 °C | 583 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | ASTM D648 |
| Glass Transition Temp, Tg | 125 °C | 257 °F | |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.4 @Frequency 1.00e+10 Hz |
3.4 @Frequency 1.00e+10 Hz |
ASTM D150 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ASTM D149 |
| Dielectric Loss Index | 0.10 @Frequency 1.00e+10 Hz |
0.10 @Frequency 1.00e+10 Hz |
ASTM D150 |
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | ASTM UL746A |
Users viewing this material also viewed the following:
- Microcell Composite Company CELLIFF® F-1020ST Polymer Foam
- SABIC Innovative Plastics Xenoy® CL101 PBT+PC (Asia Pacific)
- Saint-Gobain CHR® M705 Polyester Film Backing Acrylic Adhesive Pressure Sensitive Tape
- UBE 1022T Nylon 6 Monofilament (Drawing Ratio=5)
- Loctite® 3900 Acrylic Aerosol Coating
- DuPont Performance Polymers Sorona® 3301 BK001 Polytrimethylene Terephthalate (PTT) (Unverified Data**)&l
- Addcomp PRIEX® Ionomer 48101 PP random copolymer
- Aclo Accucomp ABS ABS804L High Impact Grade
- BASF Ultramid® B3L PA6 (Conditioned)
- Bhansali Engineering Abstron KU-650 ABS Super Heat Resistant
Copyright © lookpolymers.com All Rights Reserved